INCORPORATED WITH ASH FROM THE INCINERATION OF URBAN GARBAGE ON RED CERAMIC

INCORPORADO COM CINZAS DA INCINERAÇÃO DE LIXO URBANO EM CERÂMICA VERMELHA

Authorship

DELAQUA, GEOVANA CARLA GIRONDI; VIEIRA, CARLOS MAURÍCIO FONTES

DELAQUA, GEOVANA CARLA GIRONDI

I am this author

VIEIRA, CARLOS MAURÍCIO FONTES

I am this author

DOI

10.5151/2594-5327-41267

Downloads

Abstract

THIS WORK HAS AS ITS OBJECTIVE TO CHARACTERIZE AND TO INCORPORATE INTO A CLAY BRICK A TYPE OF WASTE, FLY-ASH, FROM THE INCINERATOR OF URBAN WASTE. THE WASTE WAS SUBMITTED TO MINERALOGICAL, PHYSICAL AND CHEMICAL CHARACTERIZATION. FORMULATIONS WERE PREPARED WITH INCORPORATION OF THE WASTE UP TO 10 WT.% INTO THE CLAYEY CERAMIC BODY. RECTANGULAR SPECIMENS WERE PREPARED BY UNIAXIAL MOLD-PRESS AT 20 MPA AND THEN FIRED IN A LABORATORY FURNACE AT 900°C. THE PHYSICAL AND MECHANICAL PROPERTIES EVALUATED WERE: PLASTICITY, LINEAR SHRINKAGE, WATER ABSORPTION AND FLEXURAL RUPTURE STRENGTH. THE RESULTS SHOWED THAT THE WASTE IS PREDOMINANTLY COMPOSED OF QUARTZ AND CALCIUM COMPOUNDS. ALTHOUGH, THE USE OF THE WASTE HAS ENHANCED THE WATER ABSORPTION OF THE CLAYEY CERAMIC, IT IS SUGGESTED TO INCORPORATE AMOUNT AROUND 5 WT.% TO AVOID DELETERIOUS EFFECT IN THE MECHANICAL STRENGTH

ESTE TRABALHO TEM COMO OBJETIVO CARACTERIZAR E INCORPORAR EM UM TIJOLO DE CERâMICO UM TIPO DE RESíDUO, CINZA VOLANTE, PROVENIENTE DO INCINERADOR DE RESíDUOS URBANOS. O RESíDUO FOI SUBMETIDO à CARACTERIZAçãO MINERALóGICA, FíSICA E QUíMICA. AS FORMULAçõES FORAM PREPARADAS COM INCORPORAçãO DO RESíDUO ATé 10% EM PESO NA MASSA CERâMICA. CORPOS DE PROVA RETANGULARES FORAM PREPARADOS POR PRENSA DE MOLDE UNIAXIAL A 20 MPA E DEPOIS QUEIMADOS EM FORNO DE LABORATóRIO A 900°C. AS PROPRIEDADES FíSICAS E MECâNICAS AVALIADAS FORAM: PLASTICIDADE, RETRAçãO LINEAR, ABSORçãO DE áGUA E RESISTêNCIA à RUPTURA FLEXãO. OS RESULTADOS MOSTRARAM QUE O RESíDUO é COMPOSTO PREDOMINANTEMENTE POR COMPOSTOS DE QUARTZO E CáLCIO. EMBORA O APROVEITAMENTO DO RESíDUO TENHA POTENCIALIZADO A ABSORçãO DE áGUA DA CERâMICA ARGILOSA, SUGERE-SE INCORPORAR QUANTIDADE EM TORNO DE 5% EM PESO PARA EVITAR EFEITO DELETéRIO NA RESISTêNCIA