Proceedings of the Seminar on Steelmaking, Casting and Non-Ferrous Metallurgy


ISSN 2594-5300

Title

INFLUÊNCIA DA PORCENTAGEM DE MAGNÉSIO E DO SUPERAQUECIMENTO NA MICROESTRUTURA DE LIGAS ALUMÍNIO- MAGNÉSIO SOLIDIFICADAS UNIDIRECIONALMENTE

INFLUENCE OF MAGNESIUM PERCENTAGE AND OVERHEATING IN THE MICROSTRUCTURE OF ALUMINUM-MAGNESIUM ALLOY

DOI

10.5151/1982-9345-30128

Downloads

Abstract

O alumínio por suas excelentes características físico químicas é empregado na indústria civil, automotiva, naval e aeroespacial. As características mecânicas dos sistemas solidificados dependem do arranjo microestrutural, mais especificamente do tamanho de grão, espaçamentos celulares ou dendríticos, das heterogeneidades de composição química, do tamanho, forma, distribuição das inclusões e das porosidades. A fusão de metais e, consequentemente, a solidificação, são etapas importantes na obtenção dos metais. Neste estudo iremos investigar a solidificação vertical ascendente em regime transiente do sistema Al-Mg. Está análise investigou experimentalmente o efeito das composições e dos superaquecimentos nas microestruturas solidificadas. Durante a fabricação dos lingotes, foram mapeadas a solidificação de cada liga. As microestruturas obtidas evidenciaram um aspecto essencialmente dendrítico, verificados através da microscopia óptica. É estabelecido no trabalho uma comparação entre os espaçamentos dendríticos primário (EDP ou λ1) e secundário (EDS ou λ2) em relação adição de 1, 3 e 5% de Mg e com patamares de superaquecimento (ΔTV) variando em 20, 40 e 60ºC.A variação do superaquecimento e da composição química dos lingotes teve influência nos espaçamentos dendríticos, verificados nas medições transversais e longitudinais dos lingotes. Para cada posição analisada foram obtidas uma média dos valores e o respectivo intervalo de dispersão.

 

Aluminum for its excellent physical and chemical characteristics is used in civil, automotive, naval and aerospace industries. The mechanical characteristics of the solidified systems depend on the microstructural arrangement, specifically grain size, cellular or dendritic spacing, heterogeneities of chemical composition, size, shape, distribution of inclusions and porosities. The melting of metal sand, consequently, solidification, are important steps in obtaining the metals. In this study we will investigate the transient ascending vertical solidification of the Al-Mg system. This analysis investigated experimentally the effect of the compositions and the superheats in the solidified microstructures. During the manufacturing of the ingots, the solidification of each alloy was mapped. The obtained microstructures evidenced essentially dendritic aspect, verified by optical microscopy. A comparison between the primary dendritic (EDP or λ1) and secondary (EDS or λ2) dendritic spacing in relation to the addition of 1, 3 and 5% Mg and with overheating (ΔTV) levels varying at 20, 40 and 60ºC. The variation of the superheating and the chemical composition of the ingots had influence in the dendritic spacing, verified in the transverse and longitudinal measurements of the ingots. For each position analyzed an average of the valuesand the respective dispersion interval.

Keywords

Ligas binarias do sistema Al-Mg, Solidificação unidirecional transiente ascendente, Microestrutura e

Binary alloys of the Al-Mg system, Ascending transient unidirectional solidification, Microstructure

How to refer

Oliveira, Eduardo Reis de; FIlho, Fernando Tadeu de Araujo; Lima, Diego Ferreira de; Vieira, Estefano Aparecido; Gomes, José Aniceto Monteiro; Filho, Claudio Alves de Siqueira; Silva, Aline Karla Barbosa da. INFLUÊNCIA DA PORCENTAGEM DE MAGNÉSIO E DO SUPERAQUECIMENTO NA MICROESTRUTURA DE LIGAS ALUMÍNIO- MAGNÉSIO SOLIDIFICADAS UNIDIRECIONALMENTE , p. 40-50. In: 48º Seminário de Aciaria, Fundição e Metalurgia de Não-Ferrosos, São Paulo, 2017.