Title

INFLUÊNCIA DA TAXA DE RESFRIAMENTO NAS TEMPERATURAS DE TRANSFORMAÇÃO E NAS MICROESTRUTURAS DE LIGAS TiNiCu COM EFEITO DE MEMÓRIA DE FORMA SOLIDIFICADAS RAPIDAMENTE

EFFECT OF THE COOLING RATE ON THE TRANSFORMATION TEMPERATURES AND MICROSTRUCTURE IN RAPIDLY SOLIDIFIED Ti-Ni-Cu SHAPE MEMORY ALLOY

Authorship

Anselmo, George Carlos dos Santos; Castro, Walman Benicio de

Anselmo, George Carlos dos Santos

I am this author

Castro, Walman Benicio de

I am this author

DOI

10.5151/1516-392X-26198

Downloads

Abstract

O efeito de memória de forma tem como principal objetivo a recuperação da forma por meio de aquecimento acima das temperaturas críticas de transformação. Fitas das ligas Ti50Ni46Cu4 e Ti50Ni44Cu6 (% at) foram preparadas através do processo melt spinnig com velocidade da roda de 38 m/s e 50 m/s. A caracterização das fitas foi feita por Calorimetria Diferencial de Varredura (DSC) e Microscopia Eletrônica de Varredura (MEV). Foi observado que com o aumento da velocidade de rotação da roda de 38 para 50 m/s um refino de grão foi observado e as temperaturas de transformação diminuíram chegando à variação de aproximadamente 7°C. A solidificação rápida produz defeitos na estrutura da liga e, consequentemente, uma maior dificuldade de ocorrer as transformações de fase, bem como produz um refino de grão.

The shape memory effect (SME) is strictly related to the reversible martensitic transformation. Shape memory characteristics of Ti50Ni46Cu4 and Ti50Ni46Cu6 (% at) alloys ribbons prepared by melt spinning were investigated by means of Differential Scanning Calorimetry (DSC) and Scanning Electronic Microscopy (SEM). In these experiments particular attention has been paid to change of the velocity of cooling wheel from 38 to 50 m/s. Then the cooling rates of ribbons were controlled. The effect of this cooling rate on austenitic and martensitic transformations behaviors is discussed. It was observed that with increasing wheel speed of 38 to 50 m/s a grain refining has been observed and the transformation temperatures decreased reaching the range of approximately 7°C. Rapid solidification produces defects in the alloy structure and, therefore, the more difficult the phase transformation occurs and produces a grain refining.

Keywords

Ligas Ti-Ni-Cu, Memória de forma, Solidificação rápida

Ni-Ti-Cu alloy, Shape memory, Rapid solidification, Melt Spinning