INFLUÊNCIA DA TEMPERATURA DE REAQUECIMENTO E DO TEMPO ENTRE PASSES NA EVOLUÇÃO MICROESTRUTURAL DE AÇOS INOXIDÁVEIS AUSTENÍTICOS

INFLUENCE OF REHEATING TEMPERATURE AND INTERPASS TIME ON THE MICROSTRUCTURAL EVOLUTION OF AUSTENITIC STAINLESS STEELS

Authorship

Silva, Mariana Beatriz dos Reis; Marrero, José Maria Cabrera; Roche, Virgine; Matias, Telma Blanco; Balancin, Oscar; Júnior, Alberto Moreira Jorge

Silva, Mariana Beatriz dos Reis

I am this author

Marrero, José Maria Cabrera

I am this author

Roche, Virgine

I am this author

Matias, Telma Blanco

I am this author

Balancin, Oscar

I am this author

Júnior, Alberto Moreira Jorge

I am this author

DOI

10.5151/1516-392X-28069

Downloads

Abstract

A influência da temperatura de reaquecimento e do tempo entre passes na evolução microestrutural dos ASTM F138 e ISO 5832-9 durante o processamento termomecânico simulado foram investigados. Ambos os materiais foram reaquecidos a 1200°C e, por comparação, o ISO 5832-9 foi reaquecido a 1250°C. As amostras foram submetidas a simulações de deformações em testes de torção com tempo entre passes de 50 e 5 s. As amostras foram caracterizadas por MO, MET, EDX, EBSD e testes de microdurezas. As curvas de tensão-deformação, a evolução microestrutural e precipitação foram analisadas e correlacionadas com o refinamento de grãos. O aço ISO 5832-9 reaquecido a 1250°C mostrou um comportamento diferente devido a maior dissolução dos precipitados.

The influence of the reheating temperature and the interpass time on the microstructural evolution of ASTM F138 and ISO 5832-9 steels during the simulated thermomechanical-processing was investigated. Both materials were reheated to 1200°C and, for comparison, ISO 5832-9 was also reheated to 1250°C. Samples were subjected to schedules of deformation by torsion testing with interpass times of 50 or 5 s. Samples were characterized by OM, TEM, EDS, EBSD and microhardness tests were also performed. The flow stress curves, microstructural evolution and precipitation were analyzed and related to grain refinement. Steel ISO 5832-9 reheated to 1250°C showed a behavior something different due to greater dissolution of precipitates.

Keywords

Processamento termomecânico, Recristalização, Nióbio

Thermomechanical processing, Recrystallization, Niobium