INFLUÊNCIA DAS FASES PRESENTES NAS MISTURAS INICIAIS E FINAIS NA EFICIÊNCIA DE DESFOSFORAÇÃO DO FERRO-GUSA

INFLUENCE OF THE PHASES PRESENT IN THE INITIAL AND FINAL MIXES IN THE DEPHOSPHORIZATION EFFICIENCY OF HOT METAL

Authorship

Berger, Anna Paula Littig; Oliveira, Daniela Bahiense de; Klippel, Cynara Christ; Scopel, Camila Santos; Silva, Felipe Lima e; Broseghini, Felipe Costa; Oliveira, José Roberto de

Berger, Anna Paula Littig

I am this author

Oliveira, Daniela Bahiense de

I am this author

Klippel, Cynara Christ

I am this author

Scopel, Camila Santos

I am this author

Silva, Felipe Lima e

I am this author

Broseghini, Felipe Costa

I am this author

Oliveira, José Roberto de

I am this author

DOI

10.5151/1982-9345-27967

Downloads

Abstract

O objetivo deste artigo é analisar a influência das fases presentes nas misturas iniciais e finais na eficiência de desfosforação do ferro-gusa. Foram realizados 8 experimentos no forno de resistência, na temperatura de 1400°C, e além disso foram feitas simulações no software FactSage 6.4. Como resultado, obteu-se que as misturas DP3 e DP4 são as mais eficientes, possuindo tanto na mistura inicial quanto na final saturação em CaO, ou seja, atividade do CaO igual a 1; atividade de FeO maior possível e maior quantidade de fase líquida possível. As misturas com fases sólidas DP5 a DP8 apresentaram menor eficiência de desfosforação, pode-se concluir então que as fases sólidas diminuem a eficiência de desfosforação em processos reais, apesar de reterem mais fósforo no equilíbrio.

The main objective of this paper is to analyze the influence of the phases present in the initial and final mixes in the dephosphorization efficiency of hot metal. Eight experiments were carried out in a resistance furnace, with temperature of 1400 ° C, and moreover simulations were performed in FactSage 6.4 software . As a result, it was obtained that DP3 and DP4 mixtures are the most efficient, having both the initial and final mixture saturation upon CaO, that is CaO activity equal to 1; FeO activity longest and largest possible amount of liquid phase. Mixtures with the solid phases DP5 and DP8 showed lower dephosphorization efficiency, then it can be concluded that these phases decrease the dephosphorization efficiency in real cases, although retaining phosphorus in equilibrium balance.

Keywords

Desfosforação, Ferro-gusa, Termodinâmica computacional

Hot metal, Dephosphorization, Computational thermodynamics