Influência do perfil de intensidade do laser na microestrutura do aço 316L produzidas por FSL

Influence of Laser Intensity Profile on the Microstructure of 316L Steel Parts Produced by slm

Authorship

ANDRADE, ANA CAROLINA GOULART DE; GONÇALVES, GABRIEL MOREIRA; NETO, AROLDO MENDES PAIVA; CABRAL, BRENO RODRIGUES; PAULO, PEDRO HENRIQUE DE CASTRO; MOZER, EUTER MARTINS; PAULA, ANDERSAN DOS SANTOS

ANDRADE, ANA CAROLINA GOULART DE

I am this author

GONÇALVES, GABRIEL MOREIRA

I am this author

NETO, AROLDO MENDES PAIVA

I am this author

CABRAL, BRENO RODRIGUES

I am this author

PAULO, PEDRO HENRIQUE DE CASTRO

I am this author

MOZER, EUTER MARTINS

I am this author

PAULA, ANDERSAN DOS SANTOS

I am this author

DOI

10.5151/5463-5463-43756

Downloads

Abstract

Neste estudo, foram comparadas amostras de aço 316L fabricadas em equipamentos de FSL do mesmo modelo, a fim de averiguar se as distinções microestruturais estavam associados ao perfil intensidade do laser (gaussiana e top-hat). A caracterização envolveu análises de microscopia óptica e eletrônica de varredura, associada a difração de elétrons retroespalhados (EBSD). As amostras processadas com perfil de laser não identificado apresentaram maior densificação, menor porosidade, poças de fusão mais definidas e grãos colunares mais grosseiros, típicos de sistemas com perfil Gaussiano, em comparação as amostras processadas top-hat. Com base nos resultados observados confrontados com a literatura, o laser não identificado era um de perfil Gaussiano, evidenciando a influência do perfil do feixe na microestrutura e qualidade das peças produzidas por FSL.

In this study, 316L steel samples manufactured on FSL equipment of the same model were compared in order to ascertain whether the microstructural differences were associated with the laser intensity profile (Gaussian and top-hat). Characterization involved optical and scanning electron microscopy analyses, associated with electron backscatter diffraction (EBSD). The samples processed with unidentified laser profile exhibited higher densification, lower porosity, more defined melt pools, and coarser columnar grains, typical of Gaussian-profile systems, compared to top-hat processed samples. Based on the observed results compared with the literature, the unidentified laser was a Gaussian profile laser, demonstrating the influence of beam profile on the microstructure and quality of SLM-produced parts.

Keywords

Fusão Seletiva a Laser, Aço 316L, Top-hat, Gaussiano

Selective Laser Melting, 316L steel, Top-hat, Gaussian