INFLUÊNCIA DOS PARÂMETROS DE TÊMPERA E REVENIMENTO SOBRE A DUREZA E A MICROESTRUTURA DO AÇO AISI M2

INFLUENCE OF QUENCHING AND TEMPERING PARAMETERS ON THE HARDNESS AND MICROSTRUCTURE OF AISI M2 STEEL

Authorship

Corrêa, Elaine Carballo Siqueira; Rosa, Júnia Bicalho Duarte; Magalhães, Aline Silva; Lopes, Wellington; Braga, Cíntia; Lourenço, Pedro Penna Coelho

Corrêa, Elaine Carballo Siqueira

I am this author

Rosa, Júnia Bicalho Duarte

I am this author

Magalhães, Aline Silva

I am this author

Lopes, Wellington

I am this author

Braga, Cíntia

I am this author

Lourenço, Pedro Penna Coelho

I am this author

DOI

10.5151/1516-392X-30530

Downloads

Abstract

Os aços rápidos são aços ferramentas de alta liga capazes de usinar metais a altas velocidades. Dentre estes, o aço rápido AISI M2 é um dos mais empregados, em função das boas propriedades alcançadas mediante a combinação de composição química e parâmetros de tratamentos térmicos. Neste contexto, o objetivo deste trabalho foi avaliar os efeitos da temperatura de aquecimento na têmpera sobre a microestrutura e dureza do aço AISI M2 após revenimento em diversas temperaturas. Para tal, duas temperaturas de têmpera e cinco temperaturas de revenimento foram definidas. As transformações microestruturais foram analisadas por meio de microscopia eletrônica de varredura e difratometria de raios-X. A dureza foi obtida por ensaios Rockwell C. Foi observado que, de modo geral, o aumento da temperatura de aquecimento promoveu elevação nos valores de dureza do aço, sendo que, para a maior temperatura utilizada, notou-se a ocorrência do fenômeno de endurecimento secundário. As análises microestruturais revelaram a presença de maior quantidade de carbonetos nas amostras temperadas à menor temperatura.

High speed steels are tool steels capable of machining metals at high speeds. Among these, the AISI M2 high speed steel is one of the most used, due to the good properties achieved through the combination of chemical composition and heat treatments parameters. The aim of this work was to evaluate the effects of quench heating temperature on the microstructure and hardness of AISI M2 steel after tempering at various temperatures. For this, two quenching temperatures and five tempering temperatures were defined. The microstructural transformations were analyzed by means of scanning electron microscopy and X-ray diffraction. The hardness was obtained by Rockwell C tests. It was observed that, in general, the increase of the heating temperature promoted an increase in the hardness values of the steel, being that, for the higher temperature used, it was noted the occurrence of the secondary hardening phenomenon. The microstructural analysis revealed the presence of a higher amount of carbides in the quenched samples at the lower temperature.

Keywords

Aço rápido, Tratamento térmico, Endurecimento secundário

High speed steel, Heat treatment, Secondary hardening