INFLUÊNCIA DA ADIÇÃO DE SÍLICA ATIVA EM PASTAS GEOPOLIMÉRICAS COM METACAULIM E CINZA VOLANTE

INFLUENCE OF THE ADDITION OF ACTIVE SILICA ON GEOPOLIMER PASTES WITH METAKAOLIN AND FLY ASH

Authorship

SILVA, SHEILA MARA SANTOS DA; BARRAZA, MADELEING TABORDA; FREITAS, JOHNATA FRANÇA FANNI; OLIVEIRA, LEANDRO BARBOSA DE; JÚNIOR, DAVI VAZ ANDRÉ; BATISTA, ISABELA DEVESA; RISCADO, ANA LAURA LOPES DE MATOS; AZEVEDO, AFONSO RANGEL GARCEZ DE; VIEIRA, CARLOS MAURÍCIO FONTES

SILVA, SHEILA MARA SANTOS DA

I am this author

BARRAZA, MADELEING TABORDA

I am this author

FREITAS, JOHNATA FRANÇA FANNI

I am this author

OLIVEIRA, LEANDRO BARBOSA DE

I am this author

JÚNIOR, DAVI VAZ ANDRÉ

I am this author

BATISTA, ISABELA DEVESA

I am this author

RISCADO, ANA LAURA LOPES DE MATOS

I am this author

AZEVEDO, AFONSO RANGEL GARCEZ DE

I am this author

VIEIRA, CARLOS MAURÍCIO FONTES

I am this author

DOI

10.5151/2594-5327-41414

Downloads

Abstract

PARA COMPREENDER O EFEITO DE MATERIAIS FINOS EM SISTEMAS GEOPOLIMéRICOS, INVESTIGOU-SE A ADIçãO DE SíLICA ATIVA EM TEORES DE 1%, 2,5% E 5% EM MASSA A UM SISTEMA BINáRIO DE METACAULIM E CINZA VOLANTE, ATIVADOS COM HIDRóXIDO E SILICATO DE SóDIO. AS MODIFICAçõES FORAM AVALIADAS NAS PASTAS TANTO NO ESTADO FRESCO QUANTO ENDURECIDO, UTILIZANDO ENSAIOS DE ESPALHAMENTO (MINI-SLUMP), VISCOSIDADE E RESISTêNCIA à COMPRESSãO EM DUAS IDADES DISTINTAS. OS RESULTADOS DEMONSTRARAM QUE A INCORPORAçãO DE SíLICA ATIVA REDUZ A TRABALHABILIDADE E AUMENTA A VISCOSIDADE DAS PASTAS. APENAS A ADIçãO DE 1% DE SíLICA ATIVA NãO RESULTOU NA DIMINUIçãO DA RESISTêNCIA à COMPRESSãO, EMBORA TENHA CONTRIBUíDO COM UM INCREMENTO DE APENAS 4%. ISSO INDICA QUE A PROPORçãO DE SIO2 NO SISTEMA é SUFICIENTE PARA PROMOVER UMA CINéTICA DE REAçãO QUE RESULTA EM UM BOM DESEMPENHO MECâNICO DO COMPóSITO.

TO UNDERSTAND THE EFFECT OF FINE MATERIALS IN GEOPOLYMERIC SYSTEMS, THE ADDITION OF SILICA FUME IN MASS PROPORTIONS OF 1%, 2.5%, AND 5% WAS INVESTIGATED IN A BINARY SYSTEM OF METAKAOLIN AND FLY ASH, ACTIVATED WITH SODIUM HYDROXIDE AND SODIUM SILICATE. THE MODIFICATIONS WERE EVALUATED IN THE PASTES IN BOTH FRESH AND HARDENED STATES, USING MINI-SLUMP, VISCOSITY AND COMPRESSIVE STRENGTH TESTS AT TWO DIFFERENT AGES. THE RESULTS DEMONSTRATED THAT THE INCORPORATION OF SILICA FUME REDUCES THE WORKABILITY AND INCREASES THE VISCOSITY OF THE PASTES. ONLY THE ADDITION OF 1% SILICA FUME DID NOT LEAD TO A DECREASE IN COMPRESSIVE STRENGTH, BUT ITS CONTRIBUTION WAS MERELY A 4% INCREASE. THIS INDICATES THAT THE PROPORTION OF SIO2 IN THE SYSTEM IS SUFFICIENT TO PROMOTE THE REACTION KINETICS THAT LEAD TO GOOD MECHANICAL PERFORMANCE OF THE COMPOSITE.

Keywords

Geopolímero; Metacaulim; Cinza volante; Sílica ativa.

Geopolymer; Metakaolin; Fly ash; Silica fume.