77º Congresso Anual da ABM - Internacional vol. 77, num.77 (2024)


Title

INFLUÊNCIA DA CINZA INFERIOR DE MADEIRA EM SUBSTITUIÇÃO PARCIAL DO CIMENTO NAS ARGAMASSAS DE REVESTIMENTO DE CIMENTO-CAL

INFLUENCE OF WOOD BOTTOM ASH ON PARTIAL REPLACEMENT OF CEMENT IN CEMENT-LIME COATING MORTARS

DOI

10.5151/2594-5327-40452

Downloads

Abstract

CINZAS INFERIORES DE MADEIRA SãO GERADAS ABUNDANTEMENTE EM PEQUENOS FORNOS E DESCARTADAS SEM CONTROLE NO SOLO. UMA POSSIBILIDADE DE APLICAçãO DESSE MATERIAL é A SUBSTITUIçãO PARCIAL DO CIMENTO EM PEQUENAS PROPORçõES NAS ARGAMASSAS. O OBJETIVO DESSA PESQUISA é AVALIAR A SUBSTITUIçãO DE CINZA INFERIOR DE MADEIRA NO CIMENTO CPIII EM ARGAMASSAS DE REVESTIMENTO, NA PROPORçãO 1:1:6 EM MASSA (CIMENTO: CAL: AREIA), UTILIZANDO 0%, 5%, 10% E 15% DA CINZA INFERIOR DE MADEIRA. PARA OBTER ESSE OBJETIVO, A CINZA INFERIOR DE MADEIRA FOI PROCESSADA E CARACTERIZADA POR: ESPECTROSCOPIA DE ENERGIA DISPERSIVA DE RAIO-X (EDX), DIFRAçãO DE RAIOS-X (DRX) E MICROSCOPIA ELETRôNICA DE VARREDURA (MEV). FOI AVALIADO NO ESTADO FRESCO A CONSISTêNCIA, E NO ESTADO ENDURECIDO FORAM AVALIADOS: RESISTêNCIA à COMPRESSãO, RESISTêNCIA à TRAçãO NA FLEXãO E MóDULO DE ELASTICIDADE DINâMICO. DENTRE OS RESULTADOS OBTIDOS, RESSALTA-SE QUE A CINZA INFERIOR DE MADEIRA PROVOCA O AUMENTO DA DEMANDA DE áGUA. ALéM DISSO, NO PERCENTUAL 5% DE SUBSTITUIçãO, AUMENTAM A RESISTêNCIA à COMPRESSãO, A RESISTêNCIA à TRAçãO NA FLEXãO E O MóDULO DE ELASTICIDADE DINâMICO. PORTANTO, O BOM DESEMPENHO DE ARGAMASSAS DE REVESTIMENTO COM CINZA INFERIOR DE MADEIRA ESTá CONDICIONADO A BAIXOS PERCENTUAIS DE SUBSTITUIçãO DO CIMENTO.

 

WOOD BOTTOM ASH IS GENERATED ABUNDANTLY IN SMALL FURNACES AND DISCARDED WITHOUT CONTROL IN THE GROUND. ONE POSSIBILITY OF APPLICATION OF THIS MATERIAL IS THE PARTIAL REPLACEMENT OF CEMENT IN SMALL PROPORTIONS IN MORTARS. THE OBJECTIVE OF THIS RESEARCH IS TO EVALUATE THE REPLACEMENT OF WOOD BOTTOM ASH IN CPIII CEMENT IN COATING MORTARS, RATIO 1:1:6 BY MASS (CEMENT: LIME: SAND), USING 0%, 5%, 10% AND 15% OF WOOD BOTTOM ASH. TO ACHIEVE THIS OBJECTIVE, WOOD BOTTOM ASH WAS PROCESSED AND CHARACTERIZED BY: ENERGY DISPERSIVE X-RAY SPECTROSCOPY (EDX), X-RAY DIFFRACTION (XRD) AND SCANNING ELECTRON MICROSCOPY (SEM). THE CONSISTENCY WAS EVALUATED IN THE FRESH STATE, AND IN THE HARDENED STATE THE FOLLOWING WERE EVALUATED: COMPRESSIVE STRENGTH, FLEXURAL STRENGTH AND DYNAMIC ELASTIC MODULUS. AMONG THE RESULTS OBTAINED, IT IS EMPHASIZED THAT WOOD BOTTOM ASH CAUSES AN INCREASE IN WATER DEMAND. FURTHERMORE, AT 5% REPLACEMENT, COMPRESSIVE STRENGTH, FLEXURAL STRENGTH AND DYNAMIC ELASTIC MODULUS OF INCREASE. THEREFORE, THE GOOD PERFORMANCE OF COATING MORTARS WITH WOOD BOTTOM ASH IS CONDITIONED BY LOW PERCENTAGES OF CEMENT REPLACEMENT.

Keywords

Cinza inferior de madeira; Substituição parcial; Argamassa de revestimento; Argamassa cimento-cal.

Wood bottom ash; Partial replacement; Coating mortar; Cement-lime mortar.