INFLUÊNCIA DA EXPOSIÇÃO TÉRMICA NA RESISTÊNCIA A COMPRESSÃO DE GEOPOLÍMEROS COM ADIÇÃO DE SÍLICA

INFLUENCE OF THERMAL EXPOSURE ON THE COMPRESSIVE STRENGTH OF GEOPOLYMERS WITH SILICA ADDITION

Authorship

BOTELHO, EMILY DE FÁTIMA PINHEIRO; FERREIRA, PAULO ANDERSON ARANHA; SANTANA, RAYANNE OLIVEIRA LEÃO; FRANÇA, GIOVANA ZAGALO DE; CANDIDO, VERÔNICA SCARPINI; SILVA, ALISSON CLAY RIOS DA

BOTELHO, EMILY DE FÁTIMA PINHEIRO

I am this author

FERREIRA, PAULO ANDERSON ARANHA

I am this author

SANTANA, RAYANNE OLIVEIRA LEÃO

I am this author

FRANÇA, GIOVANA ZAGALO DE

I am this author

CANDIDO, VERÔNICA SCARPINI

I am this author

SILVA, ALISSON CLAY RIOS DA

I am this author

DOI

10.5151/2594-4711-41567

Downloads

Abstract

OS GEOPOLíMEROS SURGIRAM DA NECESSIDADE DA INDúSTRIA CIVIL POR MATERIAIS CIMENTíCIOS MAIS SUSTENTáVEIS E COM DESEMPENHO MECâNICO SUPERIOR AO CONCRETO TRADICIONAL. RESíDUOS PROVENIENTES DE INDúSTRIAS MINERADORAS REPRESENTAM UMA VALIOSA FONTE DE SILíCIO E ALUMíNIO ESSENCIAIS PARA OS GEOPOLíMEROS. DEVIDO à SUA ESTRUTURA ALUMINOSSILICATA AMORFA, OS GEOPOLíMEROS APRESENTAM EXCELENTE RESISTêNCIA TéRMICA, E A ADIçãO DE SíLICA ELEVA SUA RESISTêNCIA MECâNICA. DIANTE DISSO, OBJETIVA-SE AVALIAR A RESISTêNCIA à COMPRESSãO DE GEOPOLíMEROS COM ADIçãO DE 4% DE SíLICA PURA APóS EXPOSIçãO TéRMICA. A PRODUçãO DOS GEOPOLíMEROS FOI REALIZADA EM MOLDES CILíNDRICOS, SEGUINDO AS DIRETRIZES DA NORMA ABNT NBR 5739:2019. OS CORPOS DE PROVA FORAM ENTãO EXPOSTOS A TEMPERATURAS DE 25°C, 200°C, 250°C E 300°C. OS RESULTADOS INDICAM QUE OS GEOPOLíMEROS COM ADIçãO DE 4% DE SíLICA PURA APRESENTARAM MELHOR RESISTêNCIA à COMPRESSãO QUANDO EXPOSTOS A 25°C. CONCLUI-SE QUE OS GEOPOLíMEROS MANTIVERAM BOA RESISTêNCIA à COMPRESSãO MESMO APóS A EXPOSIçãO TéRMICA, ESPECIALMENTE EM TEMPERATURAS MAIS BAIXAS, SUGERINDO SEU POTENCIAL PARA APLICAçõES NA CONSTRUçãO CIVIL, CONTRIBUINDO PARA MATERIAIS MAIS SUSTENTáVEIS.

GEOPOLYMERS HAVE EMERGED FROM THE CIVIL INDUSTRY'S NEED FOR MORE SUSTAINABLE CEMENTITIOUS MATERIALS WITH SUPERIOR MECHANICAL PERFORMANCE COMPARED TO TRADITIONAL CONCRETE. WASTE FROM MINING INDUSTRIES REPRESENTS A VALUABLE SOURCE OF ESSENTIAL SILICON AND ALUMINUM FOR GEOPOLYMERS. DUE TO THEIR AMORPHOUS ALUMINOSILICATE STRUCTURE, GEOPOLYMERS EXHIBIT EXCELLENT THERMAL RESISTANCE, AND THE ADDITION OF SILICA ENHANCES THEIR MECHANICAL STRENGTH. THEREFORE, THE OBJECTIVE IS TO EVALUATE THE COMPRESSION STRENGTH OF GEOPOLYMERS WITH 4% PURE SILICA ADDITION AFTER THERMAL EXPOSURE. GEOPOLYMER PRODUCTION WAS CARRIED OUT IN CYLINDRICAL MOLDS, FOLLOWING THE GUIDELINES OF THE ABNT NBR 5739:2019 STANDARD. SPECIMENS WERE THEN EXPOSED TO TEMPERATURES OF 25°C, 200°C, 250°C, AND 300°C. THE RESULTS INDICATE THAT GEOPOLYMERS WITH 4% PURE SILICA ADDITION SHOWED BETTER COMPRESSION STRENGTH WHEN EXPOSED TO 25°C. IT IS CONCLUDED THAT GEOPOLYMERS MAINTAINED GOOD COMPRESSION STRENGTH EVEN AFTER THERMAL EXPOSURE, ESPECIALLY AT LOWER TEMPERATURES, SUGGESTING THEIR POTENTIAL FOR APPLICATIONS IN THE CONSTRUCTION INDUSTRY, CONTRIBUTING TO MORE SUSTAINABLE MATERIALS.

Keywords

Geopolímeros; Sustentáveis; Resíduos; Sílica.

Geopolymers; Sustainable; Waste; Silica.