INFLUÊNCIA DA TEMPERATURA DE TRATAMENTO TÉRMICO DE UM AÇO INOXIDÁVEL AISI 430 NA DISSOLUÇÃO DE CARBONETOS DE CROMO

INFLUENCE OF HEAT TREATMENT TEMPERATURE OF AN AISI 430 STAINLESS STEEL IN CHROMIUM CARBIDES DISSOLUTION

Authorship

CORDEIRO, FABRÍCIO CÉSAR DE MENDONÇA; LABIAPARI, WILIAN DA SILVA; ALCÂNTARA, CLÁUDIO MOREIRA DE; SANTOS, LEANDRO DE ARRUDA

CORDEIRO, FABRÍCIO CÉSAR DE MENDONÇA

I am this author

LABIAPARI, WILIAN DA SILVA

I am this author

ALCÂNTARA, CLÁUDIO MOREIRA DE

I am this author

SANTOS, LEANDRO DE ARRUDA

I am this author

DOI

10.5151/2594-5327-40893

Downloads

Abstract

OS AçOS INOXIDáVEIS AISI 430 NãO ESTABILIZADOS APRESENTAM CARBONETOS DE CROMO EM SUA MICROESTRUTURA QUE FICAM DISPERSOS NA MATRIZ FERRíTICA DO AçO. DEPENDENDO DO CICLO TéRMICO A QUE O AçO é SUBMETIDO, ESTES CARBONETOS PRECIPITAM PREFERENCIALMENTE NOS CONTORNOS DE GRãOS, GERANDO UMA REGIãO EMPOBRECIDA DE CROMO EM SUAS ADJACêNCIAS EM UM PROCESSO DE SENSITIZAçãO. ESTAS REGIõES SENSITIZADAS SãO MAIS SUSCETíVEIS A ATAQUES CORROSIVOS. NESTE SENTIDO, AVALIOU-SE A DISSOLUçãO DE CARBONETOS DE CROMO NO AçO AISI 430 APóS TRATAMENTOS TéRMICOS EM DIFERENTES TEMPERATURAS. AMOSTRAS DO AçO LAMINADAS A QUENTE E RECOZIDAS FORAM TRATADAS TERMICAMENTE EM FORNO ELéTRICO E UTILIZANDO UM DILATôMETRO. AS TEMPERATURAS VARIARAM DE 750 A 1050°C, EM CICLOS DE 80S, COM RESFRIAMENTO RáPIDO. A PARTIR DE 950°C, Há UMA DIMINUIçãO DA QUANTIDADE DE CARBONETOS à MEDIDA QUE SE AUMENTA A TEMPERATURA DE TRATAMENTO TéRMICO; A PARTIR DE 1000°C, TEM-SE UM AUMENTO NA DUREZA DO MATERIAL E Há A PRESENçA DE MARTENSITA EM SUA MICROESTRUTURA, SENDO QUE A TRANSFORMAçãO DE FASE DURANTE RESFRIAMENTO OCORRE EM APROXIMADAMENTE 200°C.

NON-STABILIZED STAINLESS STEEL AISI 430 PRESENTS CHROMIUM CARBIDES IN ITS MICROSTRUCTURE THAT ARE DISPERSED IN THE FERRITIC MATRIX OF THE STEEL. DEPENDING ON THE THERMAL CYCLE USED IN THE STEEL, THESE CARBIDES PREFERENTIALLY PRECIPITATE IN GRAIN BOUNDARIES, GENERATING A REGION POUR IN CHROMIUM NEXT TO THEM, WHAT IS A SENSITIZATION PROCESS. THESE SENSITIZED REGIONS ARE MORE SUSCEPTIBLE TO CORROSIVE ATTACKS. THIS WAY, CHROMIUM CARBIDES DISSOLUTION IN AISI 430 HAD BEEN EVALUATED AFTER HEAT TREATMENTS IN DIFFERENT TEMPERATURES. HOT ROLLED AND ANNEALED SAMPLES HAD BEEN HEAT TREATED IN AN ELECTRICAL FURNACE AND USING A DILATOMETER. TEMPERATURES VARIED FROM 750 TO 1050°C, IN 80S CYCLES AND WITH FAST COOLING. FROM 950°C ON, THERE IS A DECREASE IN THE AMOUNT OF CARBIDES AS THE TEMPERATURE OF HEAT TREATMENT INCREASES. FROM 1000°C ON, THERE IS AN INCREASE IN MATERIAL HARDNESS AND MARTENSITE IS PRESENT IN THE MICROSTRUCTURE. PHASE TRANSFORMATION DURING COOLING OCCURS AROUND 200°C.

Keywords

AÇO INOXIDÁVEL; AISI 430; DISSOLUÇÃO DE CARBONETOS

Stainless steel; AISI 430; Carbides dissolution.