Title

INFLUÊNCIA DA VARIAÇÃO DA TENSÃO ENTRE PONTAS NA SOLDAGEM POR RESISTÊNCIA ELÉTRICA PARA O AÇO CARBONO AISI1065

INFLUENCE OF VOLTAGE VARIATION BETWEEN TIPS IN ELECTRIC RESISTANCE WELDING FOR AISI1065 CARBON STEEL

Authorship

SOUZA, LUCAS MENEZES DE; PEREIRA, ELAINE CRISTINA; FERNANDEZ, CAMILA VASCONCELLOS; LOPES, STHEFANIE DE CARVALHO MENDES

SOUZA, LUCAS MENEZES DE

I am this author

PEREIRA, ELAINE CRISTINA

I am this author

FERNANDEZ, CAMILA VASCONCELLOS

I am this author

LOPES, STHEFANIE DE CARVALHO MENDES

I am this author

DOI

10.5151/2594-5327-40539

Downloads

Abstract

NESTE TRABALHO FOI AVALIADA A INFLUêNCIA DA VARIAçãO DE TENSãO NO PROCESSO DE SOLDAGEM POR RESISTêNCIA ELéTRICA E DO TRATAMENTO TéRMICO REVENIDO NA MICROESTRUTURA E NAS PROPRIEDADES MECâNICAS DO AçO CARBONO AISI1065. FORAM REALIZADAS AS SOLDAGENS EM TRêS GRUPOS DE AMOSTRAS COM VARIAçõES DE TENSãO ENTRE PONTAS DE 2.0V, 2.5 V E 3.0 V PARA CADA GRUPO. APóS O PROCESSO DE SOLDAGEM, METADE DAS AMOSTRAS DE CADA GRUPO RECEBERAM O TRATAMENTO TéRMICO REVENIDO. A MICROESTRUTURA DO AçO FOI ANALISADA ANTES E APóS O PROCESSO DE TRATAMENTO TéRMICO. PARA ANáLISE DAS PROPRIEDADES MECâNICAS FORAM REALIZADOS ENSAIOS DE TRAçãO, DUREZA E MICRODUREZA. NA CARACTERIZAçãO METALOGRáFICA, VERIFICOU-SE A PRESENçA DE GRãOS ALONGADOS DE FERRITA E PERLITA NA MICROESTRUTURA DO METAL BASE. OCORREU A TRANSFORMAçãO DA MATRIZ MARTENSíTICA LOCALIZADA NA ZONA FUNDIDA E A ZONA TERMICAMENTE AFETADA EM MARTENSITA REVENIDA APóS O TRATAMENTO TéRMICO REVENIDO. FOI OBSERVADO O AUMENTO DO LIMITE DE RESISTêNCIA à TRAçãO, DUCTILIDADE E TENACIDADE NO AçO APóS REVENIDO EM COMPARAçãO AO AçO SOMENTE SOLDADO. PORéM, NA TENSãO ENTRE PONTAS DE 2.0 V APRESENTOU MELHOR COMPORTAMENTO MECâNICO APóS O TRATAMENTO TéRMICO.

IN THIS WORK, THE INFLUENCE OF VOLTAGE VARIATION IN THE RESISTANCE SPOT WELDING PROCESS AND TEMPERING HEAT TREATMENT ON THE MICROSTRUCTURE AND MECHANICAL PROPERTIES OF AISI1065 CARBON STEEL WAS EVALUATED. WELDING WAS CARRIED OUT ON THREE GROUPS OF SAMPLES WITH VOLTAGE VARIATIONS BETWEEN TIPS OF 2.0 V, 2.5 V AND 3.0 V FOR EACH GROUP. AFTER THE WELDING PROCESS, HALF OF THE SAMPLES IN EACH GROUP RECEIVED TEMPERING HEAT TREATMENT. THE MICROSTRUCTURE OF THE STEEL WAS ANALYZED BEFORE AND AFTER THE HEAT TREATMENT PROCESS. TO ANALYZE THE MECHANICAL PROPERTIES, TENSILE, HARDNESS AND MICROHARDNESS TESTS WERE CARRIED OUT. IN THE METALLOGRAPHIC CHARACTERIZATION, THE PRESENCE OF ELONGATED GRAINS OF FERRITE AND PEARLITE IN THE MICROSTRUCTURE OF THE BASE METAL WAS VERIFIED. THE TRANSFORMATION OF THE MARTENSITE MATRIX LOCATED IN THE MOLTEN ZONE AND THE HEAT-AFFECTED ZONE INTO TEMPERED MARTENSITE AFTER THE TEMPERED HEAT TREATMENT OCCURRED. AN INCREASE IN THE TENSILE STRENGTH LIMIT, DUCTILITY AND TOUGHNESS WAS OBSERVED IN THE STEEL AFTER TEMPERING COMPARED TO STEEL ONLY WELDED. HOWEVER, AT A VOLTAGE BETWEEN TIPS OF 2.0 V, IT SHOWED BETTER MECHANICAL BEHAVIOR AFTER HEAT TREATMENT.

Keywords

Aço carbono; Soldagem; Tratamento Térmico; Dureza

Carbon steel; Welding; Heat treatment; Toughness.