Title

INFLUÊNCIA DAS CARACTERÍSTICAS MICROESTRUTURAIS SOBRE AS PROPRIEDADES MAGNÉTICAS DO AÇO SILÍCIO DE GRÃO NÃO ORIENTADO 2%Si

INFLUENCE OF THE MICROSTRUCTURAL FEATURES ON THE CORE LOSS OF THE NON ORIENTED SILICON STEEL 2%Si

DOI

10.5151/1516-392X-24356

Downloads

Abstract

Neste trabalho foi determinada a influência do tamanho e da densidade de partículas sobre a perda magnética de um aço silício de grão não orientado (GNO) contendo 2%Si. Amostras provenientes de bobinas laminadas a frio após recozimento final, com dimensões de 305x30x0,54mm e teores de carbono 32 ppm e 46 ppm, foram submetidas a tratamentos de envelhecimento de 100 até 225ºC. A evolução da perda magnética durante o tratamento térmico de envelhecimento foi determinada interrompendo-se o tratamento em intervalos de tempo variados e realizando-se os testes magnéticos. Completado o ciclo de envelhecimento, todas as amostras foram avaliadas no microscópio eletrônico de varredura (MEV) para caracterização dos precipitados. Os resultados determinaram que o aumento da perda magnética ao longo do tempo, para uma dada temperatura, está associado à precipitação de carbonetos. O maior aumento da perda magnética encontrado correspondeu a uma distribuição de precipitados com tamanho médio entre 1,1 µm e 1,3 µm e a uma densidade de partículas de 0,025 partículas/µm2.

 

In this work, the influence of the average particle size and the number of particles per unit area on the core loss of the 2%Si non-oriented (NOG) silicon steel was determined. Cold rolled and annealed samples with 305x30x0,54mm with 32 ppm and 46 ppm carbon contents, were subjected to ageing treatments from 100 to 225ºC. During the ageing treatment, in each sample, the cycle was interrupted at varied time intervals in order to determine the core loss. After that, the characterization of the precipitates was performed in the scanning electron microscope (SEM). The results have revealed that the increase on core loss along the time, at each temperature, is associated with iron carbides precipitation. The maximum increase on core loss for an average particle size between 1,1 µm and 1,3 µm and for particle density of 0,025 particles/µm2.

Keywords

Aço silício GNO; Envelhecimento magnético; Características microestruturais

NOG silicon steel; Magnetic ageing; Microstructural features

How to refer

José Rogério de Oliveira Júnior; Sebastião da Costa Paolinelli; Berenice Mendonça Gonzalez; Marcela do Valle Rodrigues. INFLUÊNCIA DAS CARACTERÍSTICAS MICROESTRUTURAIS SOBRE AS PROPRIEDADES MAGNÉTICAS DO AÇO SILÍCIO DE GRÃO NÃO ORIENTADO 2%Si , p. 6284-6293. In: 69° Congresso Anual da ABM - Internacional, São Paulo - Brasil, 2014.