Title

INFLUêNCIA DE FLUXANTES NA DESFOSFORAçãO DO FERRO GUSA.

INFLUENCE OF FLUX ON THE HOT METAL DEPHOSPHORIZATION

Authorship

OLIVEIRA, JOSE ROBERTO DE; ZOTTICH, FRANKLIN DE SOUZA; NASCIMENTO, DÉBORA ZAMPIROLI DO; NOVAES, DANIEL RODRIGUES DE OLIVEIRA; SOUZA, RAPHAEL MARIANO DE; AMARAL, THIAGO BARRETO DA SILVA

OLIVEIRA, JOSE ROBERTO DE

I am this author

ZOTTICH, FRANKLIN DE SOUZA

I am this author

NASCIMENTO, DÉBORA ZAMPIROLI DO

2 Articles, Downloaded 74 Times

NOVAES, DANIEL RODRIGUES DE OLIVEIRA

I am this author

SOUZA, RAPHAEL MARIANO DE

I am this author

AMARAL, THIAGO BARRETO DA SILVA

I am this author

DOI

10.5151/2594-5300-41254

Downloads

Abstract

A MAIORIA DAS SIDERúRGICAS ENFRENTA O DESAFIO DE REDUZIR O TEOR DE FóSFORO NO AçO, O QUE SE TORNOU UM REQUISITO FUNDAMENTAL DEVIDO à CRESCENTE DEMANDA POR AçOS ESPECIAIS COM MELHORES PROPRIEDADES MECâNICAS, COMO OS UTILIZADOS NA INDúSTRIA AUTOMOTIVA. NESTE SENTIDO A DESFOSFORAçãO DE FERRO GUSA é UMA ALTERNATIVA MAIS EFICIENTE QUE A DESFOSFORAçãO DE AçO .DURANTE AO PROCESSO DE DESFOSFORAçãO, AS PRINCIPAIS FASES SóLIDAS QUE PODEM SE FORMAR NA DESFOSFORAçãO ESCóRIA SãO CAO, MGO, SILICATO DICáLCICO (2CAO.SIO2), FOSFATO TRICáLCICO (3CAO.P2O5), QUE é FORMADO PELA OXIDAçãO DO FóSFORO, E 3CAOSIO2.3CAOP2O5.NESTE SENTIDO A DESFOSFORAçãO DE FERRO GUSA é UMA ALTERNATIVA MAIS EFICIENTE . ESTE ESTUDO TEM COMO OBJETIVO AVALIAR E COMPARAR O DESEMPENHO DE DIFERENTES FUNDENTES (FLUOSPAR E CARBONATO DE SóDIO) NO FATOR DE DESFOSFORAçãO, ANALISANDO A INFLUêNCIA DAS PRINCIPAIS PROPRIEDADES E COMPOSIçãO DAS ESCóRIAS FORMADAS. PARA TANTO, FORAM ANALISADAS AS COMPOSIçõES QUíMICAS DE ESCóRIAS COM DIFERENTES TEORES DE CAO E FEO DA LITERATURA, BEM COMO DE ESCóRIAS DESFOSFORANTES PREPARADAS PARA PESQUISA. OS RESULTADOS INDICARAM AS MISTURAS DESFOSFORANTES (ESCóRIA+FLUXANTES) NAS QUAIS OCORREM AS MELHORES EFICIêNCIAS DE DESFOSFORANTES.

MOST STEEL MILLS FACE THE CHALLENGE OF REDUCING THE PHOSPHORUS CONTENT IN STEEL, WHICH HAS BECOME A FUNDAMENTAL REQUIREMENT DUE TO THE GROWING DEMAND FOR SPECIAL STEELS WITH BETTER MECHANICAL PROPERTIES, SUCH AS THOSE USED IN THE AUTOMOTIVE INDUSTRY. IN THIS SENSE, HOT METAL DEPHOSPHORIZATION IS A MORE EFFICIENT ALTERNATIVE THAN STEEL DEPHOSPHORIZATION . DURING THE DEPHOSPHORIZATION PROCESS, THE MAIN SOLID PHASES THAT CAN FORM IN THE SLAG ARE CAO, MGO, DICALCIUM SILICATE (2CAO.SIO2), TRICALCIUM PHOSPHATE (3CAO.P2O5), WHICH IS FORMED BY THE OXIDATION OF PHOSPHORUS, AND 3CAOSIO2.3CAOP2O5. THIS STUDY AIMS TO EVALUATE AND COMPARE THE PERFORMANCE OF DIFFERENT FLUXING AGENTS (FLUOSPAR AND SODA ASH) ON THE DEPHOSPHORIZATION FACTOR, ANALYZING THE INFLUENCE OF THE MAIN PROPERTIES AND COMPOSITION OF THE FORMED SLAGS. FOR THIS PURPOSE, THE CHEMICAL COMPOSITIONS OF SLAGS WITH DIFFERENT CAO AND FEO CONTENTS FROM THE LITERATURE, AS WELL AS DEPHOSPHORIZING SLAGS PREPARED FOR RESEARCH, WERE ANALYZED. THE RESULTS INDICATED THE DEPHOSPHORIZING MIXTURES (SLAG+FLUXING AGENTS) IN WHICH THE BEST DEPHOSPHORIZATION EFFICIENCIES OCCUR.

Keywords

Termodinâmica Computacional; Desfosforização; Fator de Desfosforização; Fluxantes.

Computational Thermodynamics; Dephosphorization; Dephosphorization Factor; Fluxing Agents.