Title

INFLUÊNCIA DE MACLAS E DA RUGOSIDADE SUPERFICIAL NA FORMAÇÃO DE TRINCAS DE BORDA DURANTE A LAMINAÇÃO A FRIO DE AÇOS ELÉTRICOS

INFLUENCE OF TWINS AND SURFACE ROUGHNESS ON EDGE CRACKS FORMATION DURING COLD ROLLING OF ELECTRICAL STEELS

Authorship

JÚNIOR, SÉRGIO SILVEIRA DE VASCONCELLOS; SILVA, DANIEL EUGÊNIO DA; TORRES, VICTOR FERNANDES; OLIVEIRA, PAULO RICARDO MUSSI; MORAIS, GILVAN EMILIO CASTRO; CASTRO, DIOGO FERREIRA DE

JÚNIOR, SÉRGIO SILVEIRA DE VASCONCELLOS

I am this author

SILVA, DANIEL EUGÊNIO DA

I am this author

TORRES, VICTOR FERNANDES

I am this author

OLIVEIRA, PAULO RICARDO MUSSI

I am this author

MORAIS, GILVAN EMILIO CASTRO

I am this author

CASTRO, DIOGO FERREIRA DE

I am this author

DOI

10.5151/2594-5297-40481

Downloads

Abstract

AçOS ELéTRICOS SãO USADOS NAS INDúSTRIAS DE TRANSFORMADORES E MOTORES ELéTRICOS DEVIDO A SUAS EXCELENTES PROPRIEDADES MAGNéTICAS. ESTE AçO APRESENTA FREQUENTEMENTE TRINCAS DE BORDA NA LAMINAçãO A FRIO, O QUE PODE LEVAR A RUPTURA DE TIRA E SUCATEAMENTO DO MATERIAL ACIDENTADO. ESTE TRABALHO OBJETIVOU INVESTIGAR A OCORRêNCIA DE TRINCAS DE BORDA, DURANTE A LAMINAçãO A FRIO, E SUA CORRELAçãO COM PARâMETROS, TAIS COMO MICROESTRUTURA E RUGOSIDADE SUPERFICIAL. A REDUçãO DA INTENSIDADE DE JATEAMENTO DE GRANALHAS DURANTE A DECAPAGEM MECâNICA, REDUZIU A RUGOSIDADE SUPERFICIAL E TAMBéM A OCORRêNCIA DE MACLAS, ANALISADAS POR MICROSCOPIA óPTICA. ATRAVéS DOS EXPERIMENTOS, NOTOU-SE QUE A OCORRêNCIA DAS TRINCAS NAS BORDAS é INFLUENCIADA DIRETAMENTE POR MACLAS DE DEFORMAçãO E PELA RUGOSIDADE DA SUPERFíCIE DO PRODUTO ANTES DA LAMINAçãO A FRIO.

ELECTRICAL STEELS ARE USED IN THE TRANSFORMERS AND ELECTRIC MOTORS INDUSTRY DUE TO THEIR EXCELLENT MAGNETIC PROPERTIES. THIS STEEL FREQUENTLY SHOWS EDGE CRACKS IN COLD ROLLING, WHICH MAY LEAD TO A STRIP BREAKAGE AND SCRAPPING OF THE DAMAGED MATERIAL. THIS WORK AIMED TO INVESTIGATE THE EDGE CRACK OCCURRENCE, DURING COLD ROLLING, AND ITS CORRELATION WITH PARAMETERS, SUCH AS MICROSTRUCTURE AND SURFACE ROUGHNESS. THE REDUCTION OF SHOT BLASTING INTENSITY DURING MECHANICAL PICKLING REDUCED THE SURFACE ROUGHNESS AND ALSO THE TWINS OCCURRENCE, ANALYZED THROUGH AN OPTICAL MICROSCOPE. THROUGH THE EXPERIMENTS, IT COULD BE SEEN THAT THE EDGE CRACKS OCCURRENCE IS DIRECTLY INFLUENCED BY DEFORMATION TWINS AND PRODUCT SURFACE ROUGHNESS BEFORE COLD ROLLING.

Keywords

Aços elétricos; Trincas de borda; Rugosidade; Maclas de deformação.

Electrical steel; Edge cracks; Roughness; Deformation twins.