INFLUÊNCIA DE PARÂMETRO DE SOLDAGEM NAS CARACTERÍSTICAS DA ESTRUTURA DE SOLDAGEM DE UM CORDÃO DE SOLDA PROCESSADO POR SOLDAGEM SMAW

INFLUENCE OF WELDING PARAMETER ON THE CHARACTERISTICS OF THE WELDING STRUCTURE OF A WELD BEAD PROCESSED BY SMAW WELDING

Authorship

NASCIMENTO, DAMARES DA CRUZ BARBOSA; FERREIRA, THAMIRIS DARLIENE GAMA; CANDIDO, VERÔNICA SCARPINI; NASCIMENTO, LUIZ GABRIEL DA SILVA

NASCIMENTO, DAMARES DA CRUZ BARBOSA

I am this author

FERREIRA, THAMIRIS DARLIENE GAMA

I am this author

CANDIDO, VERÔNICA SCARPINI

I am this author

NASCIMENTO, LUIZ GABRIEL DA SILVA

I am this author

DOI

10.5151/2594-5327-40472

Downloads

Abstract

A BUSCA POR MéTODOS QUE VISAM UNIR E DESENVOLVER NOVOS MATERIAIS POR AçãO DA TéCNICA DE SOLDAGEM, TORNA-SE VISADA PARA APLICAçãO INDUSTRIAL. A SOLDAGEM VISA UNIR DOIS MATERIAIS POR AçãO DA TEMPERATURA E, CONSEQUENTE FUSãO ENTRE OS MATERIAIS METáLICOS. SENDO ASSIM, OBJETIVA-SE ANALISAR A INFLUêNCIA DA CORRENTE ELéTRICA NAS CARACTERíSTICAS DO CORDãO DE SOLDA DE UMA CHAPA DE AçO DE 5/16’’. A PARTIR DOS DADOS OBTIDOS FOI POSSíVEL IDENTIFICAR OS PONTOS DE PENETRAçãO DA SOLDA, ALéM DA ZONA TéRMICA AFETADA (ZTA). PARA ANALISAR O CORDãO DE SOLDA FOI REALIZADA A ANáLISE METALOGRáFICA UTILIZANDO UM MICROSCóPIO óPTICO. OS RESULTADOS APONTARAM QUE O AUMENTO DA CORRENTE ELéTRICA TENDE A AUMENTAR PROPORCIONALMENTE PENETRAçãO DA POçA E A ZONA TERMICAMENTE. A METALOGRAFIA APONTOU O CRESCIMENTO DE GRãOS GROSSEIROS ENQUANTO Há O AUMENTO DA CORRENTE ELéTRICA FORNECIDA. A PARTIR DOS DADOS OBTIDOS PODE-SE CONCLUIR QUE A CORRENTE ELéTRICA INFLUENCIA CONTINUAMENTE NA MICROESTRUTURA DO AçO.

THE SEARCH FOR METHODS THAT AIM TO UNITE AND DEVELOP NEW MATERIALS USING THE WELDING TECHNIQUE BECOMES AIMED AT INDUSTRIAL APPLICATION. WELDING AIMS TO JOIN TWO MATERIALS BY THE ACTION OF TEMPERATURE AND, CONSEQUENTLY, FUSION BETWEEN THE METALLIC MATERIALS. THEREFORE, THE OBJECTIVE IS TO ANALYZE THE INFLUENCE OF ELECTRIC CURRENT ON THE CHARACTERISTICS OF THE WELD BEAD OF A 5/16” STEEL SHEET. FROM THE DATA OBTAINED, IT WAS POSSIBLE TO IDENTIFY THE WELD PENETRATION POINTS, IN ADDITION TO THE THERMAL AFFECTED ZONE (HAZ). TO ANALYZE THE WELD BEAD, METALLOGRAPHIC ANALYSIS WAS CARRIED OUT USING AN OPTICAL MICROSCOPE. THE RESULTS SHOWED THAT THE INCREASE IN ELECTRICAL CURRENT TENDS TO PROPORTIONALLY INCREASE PENETRATION OF THE POOL AND THE THERMAL ZONE. METALLOGRAPHY SHOWED THE GROWTH OF COARSE GRAINS WHILE THE ELECTRICAL CURRENT SUPPLIED INCREASES. FROM THE DATA OBTAINED, IT CAN BE CONCLUDED THAT THE ELECTRIC CURRENT CONTINUOUSLY INFLUENCES THE MICROSTRUCTURE OF THE STEEL.

Keywords

Soldagem; ZTA; corrente elétrica

Welding; ZTA; electric current.