INFLUÊNCIA DO MO NA PRECIPITAÇÃO DE CARBONETOS SECUNDÁRIOS NOS FERROS FUNDIDOS BRANCOS ALTO CROMO TRATADOS TERMICAMENTE EM DIFERENTES TEMPOS A 700oC

EFFECT OF MOLYBDENIUM ON THE SECONDARY CARBIDE PRECIPITATION OF HIGH CHROMIUM WHITE CAST IRON AFTER DIFFERENT HEAT TREATMENT TIMES AT 700o C

Authorship

MELLO, JOSÉ DANIEL BIASOLI DE; CARVALHO, SANDRO MAURO DE; SCANDIAN, CHERLIO; MACEDO, MARCELO CAMARGO SEVERO DE

MELLO, JOSÉ DANIEL BIASOLI DE

I am this author

CARVALHO, SANDRO MAURO DE

I am this author

SCANDIAN, CHERLIO

I am this author

MACEDO, MARCELO CAMARGO SEVERO DE

I am this author

DOI

10.5151/2594-5327-2006-15268-0465

Downloads

Abstract

Este trabalho tem como objetivo investigar o efeito do molibdênio na microestrutura de quatro ligas hipoeutéticas (20% Cr - 2,0% C, 24% Cr - 2,4% C, 20% Cr - 2,0% C -9% Mo e 24% Cr - 2,4% C - 9% Mo) e duas ligas hipereutéticas (32% Cr - 3,2% C e 32% Cr - 3,2% C-9% Mo). Todas foram submetidas a tratamento térmico na temperatura de 700oC em seis tempos diferentes (0, 1⁄2, 1, 2, 3, 4 e 5 horas) e o resfriamento foi realizado ao ar. A microestrutura foi caracterizada por microscopia óptica, além de difração de raios-X. Após o tratamento térmico de 5 horas a 700oC, foi verificada a precipitação na matriz de carbonetos secundários do tipo M7C3 para todas as ligas. A precipitação do carboneto M23C6 ocorreu para uma única composição, 20% Cr- 2,0% C - 9%Mo, a qual apresentava alguma fração de austenita no estado bruto de fusão.

This work aims to evaluate the effect of the molybdenum content on the microstructure of four hypoeutectic (20 wt% Cr - 2 wt% C and 20 wt% Cr - 2 wt% C - 9 wt% Mo) and two hypereutectic alloys (32 wt% Cr – 3.2 wt% C and 32 wt% Cr – 3.2 wt% C - 9 wt%Mo). The heat treatment was performed at 700oC in six different times (0, 1⁄2, 1, 2, 3, 4 e 5 hours) and the samples were air cooled. The microstructure was characterized by optical microscopy and X-rays diffraction. After 5 hours at 700oC, all samples show the presence of the M7C3 carbide. Besides that, the precipitation of M23C6 carbide occurs only for one composition, 20 % Cr- 2.0% C - 9%Mo, which in the as cast condition had presented some quantity of austenite.

Keywords

Tratamento térmico; Ferro fundido branco alto cromo; Molibdênio.

Heat treatment; High chromium white cast iron; Molybdenum