INFLUÊNCIA DO RAIO DA MATRIZ DE ESTAMPAGEM NO COMPORTAMENTO TRIBOLÓGIO DAS CHAPAS DE AÇO AISI 430 E ALUMÍNIO AA 1100*

INFLUENCE OF THE DRAWING DIE RADIUS ON THE TRIBOLOGICAL BEHAVIOR OF AISI 430 STEEL AND ALUMINUM AA 1100 SHEETS

Authorship

GONÇALVES, KARINA APARECIDA MARTINS BARCELOS; OLIVEIRA, EDUARDA SOARES; DAMASCENO, JULIANA RODRIGUES; NETO, ALMIR SILVA; AMARAL, ERRISTON CAMPOS; LUIZ, VALMIR DIAS

GONÇALVES, KARINA APARECIDA MARTINS BARCELOS

38 Articles, Downloaded 233 Times

OLIVEIRA, EDUARDA SOARES

I am this author

DAMASCENO, JULIANA RODRIGUES

I am this author

NETO, ALMIR SILVA

I am this author

AMARAL, ERRISTON CAMPOS

I am this author

LUIZ, VALMIR DIAS

I am this author

DOI

10.5151/5463-5463-41317

Downloads

Abstract

NA áREA DA INDúSTRIA DE CONFORMAçãO DE CHAPAS METáLICAS, OS EFEITOS CAUSADOS PELO ATRITO SãO MOTIVO DE GRANDE PREOCUPAçãO, UMA VEZ QUE IMPACTAM DIRETAMENTE NA EFICIêNCIA, QUALIDADE DO PRODUTO E DURABILIDADE DAS FERRAMENTAS UTILIZADAS NO PROCESSO DE CONFORMAçãO. ESTE ESTUDO TEM COMO OBJETIVO ANALISAR O IMPACTO DO RAIO DA MATRIZ DE ESTAMPAGEM NO COMPORTAMENTO TRIBOLóGICO DE CHAPAS DE AçO AISI 430 E ALUMíNIO AA 1100. PARA ISSO, FOI REALIZADO UM ENSAIO DE DOBRAMENTO SOB TENSãO EM TIRAS METáLICAS DE 0,8×25×750 MM, UTILIZANDO UM TRIBOSSIMULADOR EM AMBIENTE LUBRIFICADO. FORAM REALIZADAS MEDIçõES DO COEFICIENTE DE ATRITO E DA DUREZA. OS RESULTADOS OBTIDOS INDICARAM QUE O ATRITO AUMENTOU COM A DIMINUIçãO DO RAIO DO PINO DE DOBRAMENTO, NO ENTANTO, ESSE COMPORTAMENTO INVERTEU A PARTIR DE UM RAIO CRíTICO (4,5 MM), ONDE O COEFICIENTE DE ATRITO AUMENTOU COM O AUMENTO DO RAIO DO PINO. ALéM DISSO, A TIRA DE ALUMíNIO AA 1100 APRESENTOU UM COEFICIENTE DE ATRITO MAIS ELEVADO (~1,5-9,6) EM COMPARAçãO COM O AçO AISI 430. OS NíVEIS DE RUGOSIDADE E A DUREZA DAS TIRAS TENDERAM A AUMENTAR à MEDIDA QUE O RAIO AUMENTAVA.

IN THE SHEET METAL FORMING INDUSTRY, THE EFFECTS CAUSED BY FRICTION ARE OF GREAT CONCERN, AS THEY DIRECTLY IMPACT THE EFFICIENCY, PRODUCT QUALITY, AND DURABILITY OF THE TOOLS USED IN THE FORMING PROCESS. THIS STUDY AIMS TO ANALYZE THE IMPACT OF THE STAMPING DIE RADIUS ON THE TRIBOLOGICAL BEHAVIOR OF AISI 430 STEEL AND AA 1100 ALUMINUM SHEETS. TO ACHIEVE THIS, A BENDING TEST UNDER TENSION WAS CARRIED OUT ON METAL STRIPS MEASURING 0.8×25×750 MM, USING A TRIBOSIMULATOR IN A LUBRICATED ENVIRONMENT. MEASUREMENTS OF THE COEFFICIENT OF FRICTION AND HARDNESS WERE CONDUCTED. THE RESULTS INDICATED THAT FRICTION INCREASED WITH DECREASING BENDING PIN RADIUS; HOWEVER, THIS BEHAVIOR REVERSED AFTER A CRITICAL RADIUS (4.5 MM), WHERE THE FRICTION COEFFICIENT INCREASED WITH INCREASING PIN RADIUS. FURTHERMORE, THE AA 1100 ALUMINUM STRIP SHOWED A HIGHER COEFFICIENT OF FRICTION (~1.5-9.6) COMPARED TO THE AISI 430 STEEL. THE ROUGHNESS LEVELS AND HARDNESS OF THE STRIPS TENDED TO INCREASE AS THE RADIUS INCREASED.

Keywords

Conformação de chapas metálicas; Atrito; Aço AISI 430 e alumínio AA 1100; Ensaio de dobramento sob t

Sheet metal forming; Friction; AISI 430 steel and AA 1100 aluminum; Bending under tension test.