INFLUÊNCIA DO W NAS PROPRIEDADES QUÍMICAS E TENACIDADE DE AÇOS INOXIDÁVEIS SUPERDÚPLEX

INFLUENCE OF W ON CHEMICAL PROPERTIES AND TOUGHNESS OF SUPERDUPLEX STAINLESS STEELS

Authorship

Assis, Kioshy Santos de; Sousa, Flávio Vieira Vasques de; Miranda, Marcelo; Mattos, Isabel Cristina Margarit; Filho, João da Cruz Payão; Mattos, Oscar Rosa

Assis, Kioshy Santos de

I am this author

Sousa, Flávio Vieira Vasques de

I am this author

Miranda, Marcelo

I am this author

Mattos, Isabel Cristina Margarit

I am this author

Filho, João da Cruz Payão

I am this author

Mattos, Oscar Rosa

I am this author

DOI

10.5151/2594-5327-16225

Downloads

Abstract

Duas classes de aços inoxidáveis superduplex (UNS S32750 e UNS S32760) foram submetidas a tratamentos térmicos de solubilização e envelhecimento, para obtenção controlada de diferentes percentuais de fases intermetálicas deletérias. Através de metalografia quantitativa utilizando processamento de imagem (ASTM E1245-03), com auxílio de microscopia óptica e eletrônica de varredura, foi possível identificar e determinar os diferentes percentuais de fase sigma (s) obtidos. Foi utilizado o teste de impacto Charpy V (ASTM A923) para avaliar a degradação das propriedades mecânicas, devido à presença de fase s. Para verificar a resistência a corrosão localizada, as amostras foram submetidas a testes de imersão segundo a norma ASTM G48, método A. A caracterização eletroquímica foi realizada através da norma ISO 12732. O principal objetivo é analisar a influência do tungstênio na cinética de precipitação de fase s e a influência desta na susceptibilidade a corrosão localizada.

Two superduplex stainless steels (UNS S32750 and UNS S32760) were submitted to thermal aging treatments in order to obtain different levels of deleterious intermetallics phases. Through quantitative metallography using optical microscopy and scanning electronic microscopy, these phases were identified, characterized and quantified by image processing (ASTM E1245-03). We used the Charpy V impact test (ASTM A923) to assess the impairment of mechanical properties due to the presence of deleterious phases. To verify the corrosion resistance, specimens were subjected to immersion test according to ASTM G48, Method A. The electrochemical behavior of the materials was characterized with potentiodynamic reactivation, DLEPR, in accordance with procedures suggested by the ISO 12732. The goal is to verify the influence of tungsten on the kinetics of precipitation of deleterious phases and the susceptibility to localized corrosion.

Keywords

Aços UNS S32750 e UNS S32760; Tenacidade ao impacto; Fase sigma; DL-EPR.

UNS S32750 and UNS S32760 steels; Impact toughness; Sigma phase; DL-EPR.