Title

INVESTIGAçãO DA CEDAGEM EM PROCESSO DE LAMINAçãO DE AçO INOXIDáVEL AUSTENíTICO 316L

INVESTIGATION OF SAGGING IN THE ROLLING PROCESS OF CAST AUSTENITIC STAINLESS STEEL 316L

Authorship

FLEISCHHAUER, YURI DE ABREU SILVA ARAÚJO; GUZELA, LAERCIO ROSIGNOLI; COTEGIPE, FILLYPE IANG; EDUARDO, BERNARDO POMPERMAYER; RIBEIRO, RAFAELLA MARTINS; SILVA, RODRIGO VITORINO DA

FLEISCHHAUER, YURI DE ABREU SILVA ARAÚJO

I am this author

GUZELA, LAERCIO ROSIGNOLI

I am this author

COTEGIPE, FILLYPE IANG

I am this author

EDUARDO, BERNARDO POMPERMAYER

I am this author

RIBEIRO, RAFAELLA MARTINS

I am this author

SILVA, RODRIGO VITORINO DA

I am this author

DOI

10.5151/2594-5297-41457

Downloads

Abstract

A LAMINAçãO é UM DOS PROCESSOS DE CONFORMAçãO METALúRGICA MAIS IMPORTANTES. DEVIDO à SUA ALTA PRODUTIVIDADE, CERCA DE 90% DO AçO FABRICADO PASSA PELO PROCESSO DE LAMINAçãO PELO MENOS UMA VEZ DURANTE SUA PRODUçãO. NO ENTANTO, A DEFLEXãO VERTICAL DOS CILINDROS DE LAMINAçãO, CONHECIDA COMO SAGGING, AFETA A PRECISãO DA ESPESSURA DAS CHAPAS PRODUZIDAS. ASSIM, O OBJETIVO DESTE ESTUDO é INVESTIGAR O SAGGING NOS PROCESSOS DE LAMINAçãO A QUENTE E A FRIO DE UM AçO INOXIDáVEL AUSTENíTICO AISI 316L, VISANDO OBTER MAIOR PRECISãO NAS ESPESSURAS DAS PEçAS FABRICADAS. FORAM REALIZADAS SIMULAçõES COMPUTACIONAIS UTILIZANDO OS SOFTWARES THERMO-CALC E DEFORM-3D PARA DETERMINAR AS CONDIçõES DE PROCESSAMENTO. A CARACTERIZAçãO MICROESTRUTURAL FOI REALIZADA USANDO MICROSCOPIA óPTICA, MICROSCOPIA ELETRôNICA DE VARREDURA E DIFRAçãO DE RAIOS X. TESTES DE DUREZA FORNECERAM INFORMAçõES SOBRE AS PROPRIEDADES MECâNICAS. FOI POSSíVEL DETERMINAR O SAGGING PARA AS ROTAS A QUENTE E A FRIO, O QUE PERMITIU O DESENVOLVIMENTO DE ROTAS DE LAMINAçãO COM UM ALTO GRAU DE PRECISãO.

ROLLING IS ONE OF THE MOST IMPORTANT METALLURGICAL FORMING PROCESSES. DUE TO ITS HIGH PRODUCTIVITY, ABOUT 90% OF MANUFACTURED STEEL UNDERGOES THE ROLLING PROCESS AT LEAST ONCE DURING ITS PRODUCTION. HOWEVER, SAGGING, RESULTING FROM THE VERTICAL DEFLECTION OF THE ROLLING MILL ROLLS, AFFECTS THE THICKNESS ACCURACY OF THE PRODUCED SHEETS. THUS, THE AIM OF THIS STUDY IS TO INVESTIGATE SAGGING IN THE HOT AND COLD ROLLING PROCESSES OF AN AISI 316L AUSTENITIC STAINLESS STEEL, AIMING TO ACHIEVE GREATER PRECISION IN THE THICKNESSES OBTAINED IN MANUFACTURED PARTS. COMPUTATIONAL SIMULATIONS WERE PERFORMED USING THERMO-CALC AND DEFORM-3D SOFTWARE TO DETERMINE THE PROCESSING CONDITIONS. MICROSTRUCTURAL CHARACTERIZATION WAS CARRIED OUT USING OPTICAL MICROSCOPY, SCANNING ELECTRON MICROSCOPY, AND X-RAY DIFFRACTION. HARDNESS TESTS PROVIDED INFORMATION ABOUT THE MECHANICAL PROPERTIES. IT WAS POSSIBLE TO DETERMINE THE SAGGING FOR THE HOT AND COLD ROUTES, WHICH ALLOWED DESIGNING ROLLING ROUTES WITH A HIGH DEGREE OF PRECISION.

Keywords

lamiação; cedagem; retorno elástico; thermo-calc

Rolling; Sagging; Springback; Thermo-Calc.