LEVANTAMENTO DA CURVA TTT DO AÇO 15B30 COM ANÁLISE DOS CONSTITUINTES FERRITA E PERLITA

DETERMINATION OF THE FERRITE AND PERLITE TTT DIAGRAM OF 15B30 STEEL

DOI

10.5151/2594-5327-22880

Downloads

Abstract

O estudo proposto teve como objetivo determinar as curvas TTT (temperatura, tempo e transformação), dos constituintes ferrita e perlita do aço 15B30. O trabalho foi realizado por meio de análises de microscopia de diversas amostras, previamente austenitizadas, que foram submetidas a diferentes tratamentos isotérmicos da região de formação de ferrita e perlita. Para a escolha das temperaturas e tempos de trabalho fez-se o esboço da curva TTT do aço em estudo com o auxílio do programa Stecal 3.0. Um objetivo secundário é o de validar a curva TTT esboçada pelo programa Stecal 3.0. Observou-se que é possível o levantamento da curva TTT do aço 15B30 partindo-se da escolha das variáveis de trabalho através da curva prevista pelo software Stecal 3.0 e por meio de análises de microscopia, porém deve-se medir previamente o tamanho de grão austenítico da matéria-prima e é necessário o controle de temperatura do banho de sal com o auxílio de um termopar para correta determinação da real temperatura de transformação isotérmica.

 

The study proposed aims the determination of the TTT diagram (temperature, time and transformation), of ferrite and perlite of 15B30 steel. The study has been done through microscopy analysis of various samples, previously austenitized and submitted to different isothermal treatments in the region of ferrite and perlite formation. Temperatures and times choices were made up the TTT diagram outlined of the steel in study with the help of the Stecal 3.0 software. A secondary objective is to certify the TTT diagram outlined with the Stecal 3.0 program. It was observed that it’s possible to determine the 15B30 steel TTT diagram choosing the variables through the curve outlined by Stecal 3.0 and through microscopy analysis, but the prior austenitic grain size should be measured and it is necessary to control the salt bath temperature with the aid of a thermocouple for a better determination of the exact isothermal transformation temperature.

Keywords

Aço AISI 15B30; Temperabilidade; Transformação de fases.

AISI 15B30 steel; Hardenability; Phase quantification; Phase transformation.