MATERIAIS COMPÓSITOS DE MATRIZ POLIÉSTER REFORÇADO COM RESÍDUOS DE MADEIRA E FIBRAS DE SISAL DE COMPRIMENTO HÍBRIDO COM VARIAÇÃO DE 5 A 15 mm

MATRIX COMPOSITE MATERIALS REINFORCED POLYESTER WASTE WOOD AND FIBER LENGTH OF SISAL HYBRID WITH VARIATION OF 5 TO 15 mm

Authorship

Santos, Jhonatan de Almeida dos; Kuwahara, Moacir; Santos, Izael Pinho dos; Santos, Charles Aran Sabel dos; Pereira, Leo Cesar de Oliveira; Lopes, Carlos Eduardo Pinto; Santos, Eduardo Jesus Siva dos; Costa, Deibson Silva da; Banna, Wassim Raja El; Fujiyama, Roberto Tetsuo

Santos, Jhonatan de Almeida dos

I am this author

Kuwahara, Moacir

I am this author

Santos, Izael Pinho dos

I am this author

Santos, Charles Aran Sabel dos

I am this author

Pereira, Leo Cesar de Oliveira

I am this author

Lopes, Carlos Eduardo Pinto

I am this author

Santos, Eduardo Jesus Siva dos

I am this author

Costa, Deibson Silva da

I am this author

Banna, Wassim Raja El

I am this author

Fujiyama, Roberto Tetsuo

I am this author

DOI

10.5151/2594-5327-23526

Downloads

Abstract

O presente trabalho emprega materiais compósitos de matriz poliéster reforçados por fibras curtas de sisal e resíduo de madeira dispostos aleatoriamente. Utilizando, para isto, o menor nível possível de processamento tecnológico nas etapas produtivas. A matriz utilizada foi a resina poliéster tereftálatica insaturada e pré-acelerada, sob a denominação comercial de Deverlopy 754, tendo como agente de cura o Butanox M- 50, obedecendo à proporção de 0,33% (v/v). As fibras de sisal foram cortadas com uso de um moinho granulador produzindo comprimentos que variam de 5 a 15 mm. O resíduo de madeira utilizado foi o de Angelim Pedra (Hymenolobium petraeum), obtido no mercado local e submetido a processo de peneiramento. As propriedades mecânicas analisadas por ensaios de tração e as superfícies de fratura geradas avaliadas por microscopia estereoscópica de modo a se correlacionar os aspectos de fratura com as propriedades mecânicas.

This study employs polyester matrix composites reinforced with short fibers of sisal, wood waste randomly arranged. Using, for this, the lowest possible level of technological processes in the production stages. The matrix used was tereftálatica unsaturated polyester resin and preaccelerated under the tradename Deverlopy 754, having as the curing agent Butanox M-50, according to the proportion of 0.33% (v / v). The sisal fibers were cut using a granulator mill producing lengths ranging from 5 to 15 mm. The wood waste was used Angelim Stone (Hymenolobium petraeum) obtained in the local market and subjected to screening process. The mechanical properties by tensile and fracture surfaces generated evaluated by stereoscopic microscopy to correlate with aspects of fracture mechanical properties.

Keywords

Fibras de sisal; Resíduos de madeira; Materiais compósitos.

Sisal fibers; Wood waste; Composite materials.