Title

MATERIAL COMPÓSITO DE MATRIZ POLIÉSTER REFORÇADA COM FIBRAS DE ALGODÃO CONTÍNUAS E ALINHADA

COMPOSITE MATERIAL OF POLYESTER MATRIX REINFORCED WITH COTTON FIBER CONTINUED AND ALIGNED

Authorship

DOI

10.5151/2594-5327-22950

Downloads

339 Downloads

Abstract

Este trabalho apresenta os procedimentos desenvolvidos para a fabricação de compósitos poliméricos de matriz poliéster reforçados por fibras de algodão. Essas fibras são bastante abundantes na região Amazônica. Antes da fabricação do compósito foi realizado o processo de alinhamento manual das fibras. Já o processo de manufatura do compósito, a priori, foi realizado a preparação da matriz, através da adição de catalisador e Cobalto na resina polimérica e depois espalhada na fibra. Por último, o compósito foi submetido a uma prensa hidráulica a 5 kN, em seguida foi retirado e cortado de acordo com a norma ASTM D 3039, para a realização do ensaio de tração. Por último, foi realizado o ensaio individual das fibras, seguindo a norma ASTM D 3822. As fibras de algodão apresentaram resistência mecânica entre 226,511 e 391,002 MPa. O compósito apresentou resistência mecânica média de 34,276 MPa. Os resultados foram comparados com valores existentes na literatura.

 

This work presents the procedures to manufacture polyester matrix polymer composites reinforced with cotton fibers. These fibers are quite abundant in the Amazon region. Before to the manufacture of composite it was realized manual alignment of the fibers. Already the manufacturing process of the composite, at first, it was realized the preparation of matrix, by adding catalyzer, cobalt and the polymeric resin, then spread over the fiber. Finally, the composite is submitted in a hydraulic press at 5 kN then was removed and cut according to ASTM D 3039, to achieve the tensile test. Finally, another test was performed individual fibers, according to ASTM D 3822. Cotton fibers had mechanical resistance between 226.511 and 391.002 MPa. The composite had an average mechanical resistance of 34.276 MPa. The results obtained were compared with existing values at current literature.

Keywords

Compósitos; Fibras vegetais; Laminados; Propriedade mecânicas.

Composite; Vegetable fibers; Laminated; Mechanical properties.