MELHORIA DO DESEMPENHO EM ALTA TEMPERATURA DO AÇO 9CR COM ADIÇÕES DE TUNGSTÊNIO E TÂNTALO

ENHANCEMENT HIGH TEMPERATURE PERFORMANCE OF 9CR STEEL WITH TUNGSTEN AND TANTALUM ADDITIONS

Authorship

GARCIA, JULIANNA MAGALHÃES; NASCIMENTO, MARVIN DO; BEVICTORI, ANDRE LUIZ LEAL; SOUSA, TALITA GAMA DE; BRANDÃO, LUIZ PAULO MENDONÇA

GARCIA, JULIANNA MAGALHÃES

I am this author

NASCIMENTO, MARVIN DO

I am this author

BEVICTORI, ANDRE LUIZ LEAL

I am this author

SOUSA, TALITA GAMA DE

I am this author

BRANDÃO, LUIZ PAULO MENDONÇA

I am this author

DOI

10.5151/Fault-41202

Downloads

Abstract

A SELEçãO APROPRIADA DE MATERIAIS é CRUCIAL PARA GARANTIR A EFICáCIA E LONGEVIDADE DOS COMPONENTES EM AMBIENTES EXTREMOS. ESTE ESTUDO FOCA NO AçO 9CR, APRIMORADO COM ADIçõES DE TUNGSTêNIO (W) E TâNTALO (TA) PARA MELHORAR AS PROPRIEDADES MECâNICAS E A RESISTêNCIA à CORROSãO. AS ADIçõES DE W E TA FORMAM CARBONETOS ESTáVEIS, COMO M23C6 E TAC, QUE AUMENTAM A RESISTêNCIA à FLUêNCIA E A ESTABILIDADE à OXIDAçãO EM ALTAS TEMPERATURAS. ENSAIOS DE TRAçãO A TEMPERATURA AMBIENTE E A 625°C, JUNTAMENTE COM ANáLISES MICROESTRUTURAIS E DE FRATURA, REVELAM QUE O AçO 9CR MODIFICADO APRESENTA MELHORIAS SIGNIFICATIVAS NO LIMITE DE ESCOAMENTO (σY) E NA RESISTêNCIA à TRAçãO (σUTS) EM COMPARAçãO COM O AçO 9CR COMERCIAL. ESSES APRIMORAMENTOS SãO ATRIBUíDOS à FINA DISPERSãO DE CARBONETOS QUE IMPEDEM O MOVIMENTO DAS DISCORDâNCIAS, DEMONSTRANDO A ADEQUAçãO DO MATERIAL PARA APLICAçõES EM ALTAS TEMPERATURAS EM PLANTAS DE ENERGIA.

THE APPROPRIATE SELECTION OF MATERIALS IS CRUCIAL FOR ENSURING THE EFFECTIVENESS AND LONGEVITY OF COMPONENTS IN EXTREME ENVIRONMENTS. THIS STUDY FOCUSES ON 9CR STEEL, ENHANCED WITH TUNGSTEN (W) AND TANTALUM (TA), TO IMPROVE MECHANICAL PROPERTIES AND CORROSION RESISTANCE. THE ADDITIONS OF W AND TA FORM STABLE CARBIDES, SUCH AS M23C6 AND TAC, WHICH INCREASE CREEP RESISTANCE AND OXIDATION STABILITY AT HIGH TEMPERATURES. TENSILE TESTS AT ROOM TEMPERATURE AND 625°C, ALONG WITH MICROSTRUCTURAL AND FRACTURE ANALYSES, REVEAL THAT THE MODIFIED 9CR STEEL EXHIBITS SIGNIFICANT IMPROVEMENTS IN YIELD STRENGTH (σY) AND ULTIMATE TENSILE STRENGTH (σUTS) COMPARED TO COMMERCIAL 9CR STEEL. THESE ENHANCEMENTS ARE ATTRIBUTED TO THE FINE DISPERSION OF CARBIDES THAT PREVENT DISLOCATION MOVEMENT, DEMONSTRATING THE MATERIAL SUITABILITY FOR HIGH-TEMPERATURE APPLICATIONS IN POWER PLANTS.

Keywords

9Cr; M23C6; TaC; Resistência mecânica

9Cr; M23C6; TaC; Mechanical resistance.