Title

MODELAGEM DE CURVAS DE FLUXO PARA AÇO LIVRE- DE-INTERSTICIAL E MUITO BAIXO CARBONO NA REGIÃO FERRÍTICA

MODELING OF FLOW CURVES OF IF AND VERY LOW CARBON STEEL IN THE FERRITIC PHASE

Authorship

Vilela, Jefferson José; Carneiro, José Rubens Gonçalves; Barbosa, Ronaldo

Vilela, Jefferson José

I am this author

Carneiro, José Rubens Gonçalves

I am this author

Barbosa, Ronaldo

I am this author

DOI

10.5151/2594-5297-0040

Downloads

Abstract

Os esquemas de conformação (seqüência de passes, temperatura, velocidade de deformação e tempos entre passes) são projetados através de modelos que prevêem as cargas de conformação e a evolução microestrutural durante o processo de laminação a morno. Esses modelos são obtidos através de curvas de fluxo em condições ideais, onde a temperatura e a velocidade de deformação são constantes. O objetivo desta pesquisa foi modelar matematicamente a curva de fluxo de dois aços, sendo um deles livre-de-intersticial (LI) ao titânio e outro muito baixo carbono e envelhecível. Os pontos experimentais necessários ao desenvolvimento do modelo foram obtidos através de ensaio de torção, nas temperaturas de 650 a 800 °C e velocidades de deformação de 0,1 a 10 s . Os mecanismos de amaciamento dinâmico dos aços LI foram estudados indiretamente através das curvas de fluxo. A curva

Models that foresee load and microstructures during warm rolling are used in design of the forming schedules (deformation per pass, temperature, rate strain and interpass time). These models are obtained from flow curves that are measured under ideal conditions where temperatures and strain rates are constant. The objective in this work was to model flow curves of interstitial free (IF) and very low carbon steel, one of them Ti stabilized. The form of curves indicates that dynamic recrystallization occurred in both alloys. The data used in the model that was obtained from torsion tests in temperatures ranging from 650 to 800 °C and strain rates from 0.1 to 10 s . Measurement of the softening dynamic mechanisms occurring during deformation of the IF steels were obtained by indirect evaluation of flow curves. The dynamic recrystallization outset was obtained by measuring the critical strain (

Keywords

Equações constitutivas; Recristalização dinâmica; Ferrita; Aços livres-de-intersticial.

Constitutive equation; Dynamic recrystallization; Ferrite; IF steel.