Title

NANOPARTÍCULAS DE NÍQUEL-ZINCO NA PRODUÇÃO DE CERÂMICAS COM CAVIDADES POROSAS ORIENTADAS

NICKEL-ZINC NANOPARTICLES IN THE PRODUCTION OF CERAMICS WITH ORIENTED POROUS CAVITIES

Authorship

CARVALHO, BRUNO CRISTIAN MELLO; FARIA, SABRINA COSTA; RIBEIRO, JULIANA LOPES; MORAES, FELLIPE DE SÁ; ALVES, DIEGO DOS SANTOS; JÚNIOR, EUSTÁQUIO DE SOUZA BAÊTA; AGUILERA, LETICIA DOS SANTOS

CARVALHO, BRUNO CRISTIAN MELLO

I am this author

FARIA, SABRINA COSTA

I am this author

RIBEIRO, JULIANA LOPES

I am this author

MORAES, FELLIPE DE SÁ

I am this author

ALVES, DIEGO DOS SANTOS

I am this author

JÚNIOR, EUSTÁQUIO DE SOUZA BAÊTA

I am this author

AGUILERA, LETICIA DOS SANTOS

32 Articles, Downloaded 167 Times

DOI

10.5151/2594-4711-40825

Downloads

Abstract

POROSIDADE CONTROLADA é UMA PROPRIEDADE DE INTERESSE PARA ESTUDOS EM APLICAçõES COMO FILTROS, CATALISADORES, ABSORVEDORES. EM PROCESSAMENTO DE MATERIAIS, A TéCNICA DE FREEZE CASTING OFERECE GRANDE VERSATILIDADE DE PEçAS A SEREM PRODUZIDAS EM RELAçãO àS DIMENSõES, TIPO DE MATERIAIS E CARACTERíSTICAS ESTRUTURAIS DAS CAVIDADES POROSAS FORMADAS. NESTE TRABALHO, A FERRITA MISTA DE NíQUEL-ZINCO FOI UTILIZADA COMO CARGA SóLIDA DE SUSPENSãO COLOIDAL PRECURSORA DO PROCESSAMENTO DE FREEZE CASTING. AS MACRO E MICRO ESTRUTURAS POROSAS FORMADA NO PROCESSAMENTO FOI INVESTIGADA POR MéTODO DE ARQUIMEDES E POR MICROSCOPIA ELETRôNICA DE VARREDURA (MEV) BUSCANDO COMPARAR CARACTERíSTICAS OBTIDAS PELA VARIAçãO DE TRêS LIGANTES POLIMéRICOS, O PEG-400, 1500 E 4000 COM CONCENTRAçãO DE 4%. FORAM OBSERVADAS POROSIDADES ALTAS, EM TORNO DE 70% PARA AS TRêS AMOSTRAS E AS IMAGENS DE MEV REVELARAM UMA ESTRUTURA TíPICA DE CONGELAMENTOS EM ALTAS TAXAS DE RESFRIAMENTO, ALéM DA ESTRUTURA COLUNAR DE INTERESSE MAIS PRONUNCIADA E POROS MAIS LARGOS E HOMOGêNEOS NA AMOSTRA COM PEG-4000, EMBORA AS TRêS VARIAçõES APRESENTARAM A ESTRUTURA SATISFATORIAMENTE.

CONTROLLED POROSITY IS A PROPERTY OF INTEREST FOR STUDIES IN APPLICATIONS SUCH AS FILTERS, CATALYSTS, ABSORBERS. IN MATERIALS PROCESSING, THE FREEZE CASTING TECHNIQUE OFFERS GREAT VERSATILITY OF PARTS TO BE PRODUCED IN RELATION TO THE DIMENSIONS, TYPE OF MATERIALS AND STRUCTURAL CHARACTERISTICS OF THE POROUS CAVITIES FORMED. IN THIS WORK, MIXED NICKEL-ZINC FERRITE WAS USED AS A SOLID FILLER FOR COLLOIDAL SUSPENSION AS A PRECURSOR TO FREEZE CASTING PROCESSING. THE MACRO AND MICRO POROUS STRUCTURES FORMED DURING PROCESSING WERE INVESTIGATED USING THE ARCHIMEDES METHOD AND SCANNING ELECTRON MICROSCOPY (SEM) SEEKING TO COMPARE CHARACTERISTICS OBTAINED BY VARYING THREE POLYMERIC LIGANDS, PEG-400, 1500 AND 4000 WITH A CONCENTRATION OF 4%. HIGH POROSITIES WERE OBSERVED, AROUND 70% FOR THE THREE SAMPLES AND THE SEM IMAGES REVEALED A STRUCTURE TYPICAL OF FREEZING AT HIGH COOLING RATES, IN ADDITION TO THE MORE PRONOUNCED COLUMNAR STRUCTURE OF INTEREST AND WIDER AND MORE HOMOGENEOUS PORES IN THE SAMPLE WITH PEG- 4000, ALTHOUGH THE THREE VARIATIONS PRESENTED THE STRUCTURE SATISFACTORILY.

Keywords

Ferrita de níquel-zinco; Porosidade; Freeze-casting; Polietilenoglicol.

Nickel-zinc ferrite; Porosity; Freeze-casting; Polyethylene glycol.