Title

NITRETAÇÃO A PLASMA TRIODO D.C E RECOBRIMENTO PVD DE AÇO ULTRA-BAIXO CARBONO (UBC): INFLUÊNCIA NO COMPORTAMENTO À CORROSÃO COMPARADA À DO AÇO GALVANIZADO

D.C TRIODE PLASMA NITRIDING AND PVD COATING OF ULTRA-LOW CARBON (ULC) STEEL: EFFECTS ON CORROSION BEHAVIOR COMPARED TO GALVANIZED STEELS

Authorship

Leyva, Carlos Alberto Llanes; Godoy, Geralda Cristina Durães de; Schvartzman, Monica; Bozzi, Antônio César

Leyva, Carlos Alberto Llanes

I am this author

Godoy, Geralda Cristina Durães de

I am this author

Schvartzman, Monica

I am this author

Bozzi, Antônio César

I am this author

DOI

10.5151/2594-5327-21290

Downloads

Abstract

Neste trabalho foi investigado o comportamento à corrosão de aço ultra-baixo carbono estabilizado com Ti, após Nitretação a Plasma Triodo D.C (DC-TPN) e recobrimento seqüencial com CrAlN a Plasma por Deposição Física de Vapor com Feixe de Elétrons (EB-PAPVD). Os processos de fabricação são descritos. O substrato de aço UBC, o aço nitretado e o correspondente sistema dúplex com CrAlN foram estudados. Os resultados de ensaios de corrosão dos sistemas modificados a plasma foram comparados com o aço não tratado e com o aço galvanizado e eletrogalvanizado. Esses resultados indicam que é viável a fabricação de sistema dúplex em UBC-Ti via DC-TPN e EB-PAPVD com ganho na resistência à corrosão. As curvas potenciodinâmicas claramente se deslocaram para potenciais de corrosão mais altos e intensidades de corrosão menores, para o sistema dúplex comparado ao substrato não tratado ou galvanizado.

The characterization and corrosion behavior of Ti-stabilized Ultra-Low Carbon (ULC) steel after surface modification by D.C Triode Plasma Nitriding (DC-TPN) and sequential coating with CrAlN by Electron Beam Plasma Assisted Physical Vapor Deposition (EB-PAPVD) were investigated. Manufacturing processes were described. The ULC steel substrate, the nitrided steel and the corresponding CrAlN duplex were studied. Results from corrosion tests of plasma-modified systems were compared to those from uncoated, electro-galvanized and galvannealed ULC steel sheets. Results indicate that it is feasible to manufacture duplex Ti-ULC steel via DCTPN and EB-PAPVD with actual improvement of the corrosion resistance. Potentiodynamic curves clearly showed a shift to higher corrosion potentials and lower corrosion current intensity from the untreated ULC substrate to the duplex system.

Keywords

Ti-stabilized ultra-low carbon steel; Corrosion resistance; Duplex coating.

Aço ultra-baixo carbono; Resistência à corrosão; Recobrimento duplex.