Title

OTIMIZAÇÃO DO REVESTIMENTO REFRATÁRIO DE MGO-C VISANDO MELHOR COMPORTAMENTO TERMOMECÂNICO E REDUÇÃO DE TRINCAS VERTICAIS EM PANELA DE AÇO

OPTIMIZATION OF MGO-C REFRACTORY LINING AIMING FOR BETTER THERMOMECHANICAL BEHAVIOR AND REDUCTION OF VERTICAL CRACKS IN STEEL LADLE

Authorship

PAULA, THALES FONSECA DE; SILVA, SERGIO LUIZ CABRAL DA; MARTINS, LEANDRO ROCHA; MENEZES, PEDRO LUIZ FONSECA; MARIZ, RODRIGO LIMA; MACEDO, SOPHIA VIEIRA DE

PAULA, THALES FONSECA DE

I am this author

SILVA, SERGIO LUIZ CABRAL DA

I am this author

MARTINS, LEANDRO ROCHA

I am this author

MENEZES, PEDRO LUIZ FONSECA

I am this author

MARIZ, RODRIGO LIMA

I am this author

MACEDO, SOPHIA VIEIRA DE

I am this author

DOI

10.5151/2594-5327-41133

Downloads

Abstract

DENTRE OS MECANISMOS DE DESGASTE DO REVESTIMENTO REFRATáRIO EM PANELA DE AçO REVESTIDAS COM REFRATáRIO DA LINHA MAGNéSIA-CARBONO, AS TRINCAS VERTICAIS NAS PAREDES DA PANELA APRESENTAM-SE COM FREQUêNCIA DEMANDANDO SOLUçãO PARA MINIMIZAR ESTE TIPO DE DESGASTE. COM ESTE OBJETIVO FOI REALIZADO NO CENTRO DE PESQUISA DA RHI MAGNESITA UM ESTUDO FOCADO NO SISTEMA LIGANTE DO MATERIAL REFRATáRIO, PARTINDO DA UTILIZAçãO DE LIGANTE A BASE DE RESINA, QUE PROPORCIONA RIGIDEZ ELEVADA AO MATERIAL REFRATáRIO, PARA UMA COMBINAçãO DE PICHE ECOLóGICO COM RESINA. ESTE SISTEMA LIGANTE PROPORCIONA MELHOR COMPORTAMENTO TERMOMECâNICO AO MATERIAL, BEM COMO REDUçãO DE EMISSõES DE VOLáTEIS DURANTE O AQUECIMENTO DA PANELA, CONTRIBUINDO PARA O CONTROLE DE EMISSõES. ESSE PRODUTO FOI TESTADO NA LINHA DE METAL DE PANELAS DE AçO. OS RESULTADOS FORAM POSITIVOS EM RELAçãO à REDUçãO DAS TRINCAS VERTICAIS DO REVESTIMENTO, E NA REDUçãO NAS EMISSõES DE VOLáTEIS, LEVANDO A UMA MELHORIA NA PERFORMANCE DO REVESTIMENTO DA PANELA.

AMONG THE WEAR MECHANISMS OF THE REFRACTORY LINING IN STEEL LADLES COATED WITH MAGNESIA-CARBON REFRACTORY, VERTICAL CRACKS IN THE LADLE WALLS ARE FREQUENTLY PRESENT, REQUIRING A SOLUTION TO MINIMIZE THIS TYPE OF WEAR. WITH THIS OBJECTIVE, A STUDY WAS CARRIED OUT AT THE RHI MAGNESITA RESEARCH CENTER FOCUSED ON THE BINDING SYSTEM OF THE REFRACTORY MATERIAL, STARTING FROM THE USE OF A RESIN-BASED BINDER, WHICH PROVIDES HIGH RIGIDITY TO THE REFRACTORY MATERIAL, FOR A COMBINATION OF ECOLOGICAL TAR WITH RESIN. THIS BINDING SYSTEM PROVIDES BETTER THERMOMECHANICAL BEHAVIOR TO THE MATERIAL, AS WELL AS REDUCING VOLATILE EMISSIONS DURING HEATING OF THE LADLE, CONTRIBUTING TO THE CONTROL OF POLLUTANT EMISSIONS. THIS PRODUCT WAS TESTED IN THE METAL LINE OF STEEL LADLES. THE RESULTS WERE POSITIVE IN RELATION TO THE REDUCTION OF VERTICAL CRACKS IN THE LINING, AND THE REDUCTION IN VOLATILE EMISSIONS, LEADING TO AN IMPROVEMENT IN THE PERFORMANCE OF THE LADLE LINING

Keywords

Panela de Aço; Sistema ligante de Refratário; Refratário Magnésia Carbono

Steel Ladle; Refractory binder system; Magnesia carbon refractory.