Title

POLIMENTO ELETROQUÍMICO DE AÇOS INOXIDÁVEIS ABNT 304 EM SOLUÇÃO CONCENTRADA DE ÁCIDOS SULFÚRICO E CRÔMICO

ELETROPOLISHING OF ABNT 304 STAINLESS STEEL IN CONCENTRADED SOLUTION OF SULFURIC AND CHROMIC ACIDS

Authorship

Santos, Marta Ribeiro dos; Duarte, Michelle Cristiane da Silva; Junqueira, Rosa Maria Rabelo

Santos, Marta Ribeiro dos

I am this author

Duarte, Michelle Cristiane da Silva

I am this author

Junqueira, Rosa Maria Rabelo

I am this author

DOI

10.5151/2594-5297-15741

Downloads

Abstract

Neste trabalho, foram realizados estudos sobre o uso de uma solução 2,5M CrO3 + 5,0M H2SO4, utilizada no processo de coloração industrial de aços inoxidáveis, como solução eletrolítica para efetuar eletropolimento desses materiais. Foram avaliados os efeitos da temperatura e do tempo de polimento sobre a refletância, rugosidade e resistência à corrosão de aços inoxidáveis ABNT 304 com acabamento superficial tipo BB (Bright Buffing). Foi observado que o polimento realizado à temperatura ambiente aumentou a refletividade do aço. A rugosidade das amostras polidas em relação ao material como recebido aumentou embora tenha apresentado grande dispersão. O polimento eletroquímico na solução sulfocrômica não modificou a resistência à corrosão do aço ABNT 304.

In this work, the use of an 2.5M CrO3 + 5.0M H2SO4 electrolitic solution, employed in electrochemical coloration of stainless steels, was evaluated as electrolyte for eletropolishing these materials. The effect of time and temperature polishing on the reflectance, roughness and corrosion resistance of a Bright Buffing ABNT 304 stainless steel were investigated. It was shown that the reflectivity was improved when the steel was electropolished at room temperature. The surface roughness of the polished samples have increased when compared with the “as received” sample., even though a high data scattering was observed. A comparison between the material corrosion resistance before and after the eletropolishing was performed and it was observed that this process did not influence the corrosion resistance of the AISI 304 stainless steel.

Keywords

Aço inoxidável austenítico; Polimento eletrolítico; Solução sulfocrômica; Resistência à corrosão.

Austenitic stainless steel; Electrolitic polishing; Sulphochromic solution; Corrosion resistance.