PREDIÇÃO DA PRECIPITAÇÃO COM BASE NA TERMODINÂMICA COMPUTACIONAL PARA AÇOS BAIXO CARBONO MICROLIGADOS

DETERMINATION OF TRANSFORMATION TEMPERATURES A1 AND A3 BY COMPUTATIONAL THERMODYNAMICS AND EMPIRICAL EQUATIONS

DOI

10.5151/2594-5297-24025

Downloads

Abstract

Esse trabalho tem por objetivo mostrar os tipos de precipitados formados em aços baixo carbono microligados ao Nb com adição de manganês e também a sequência de precipitação desses compostos. Para a realização dos mapas de precipitação foi utilizado o programa thermocalc na versão 5 do windows (TCFW5) com banco de dados do Fe na versão 6 do programa (TCFE6). Com base nos estudos termodinâmicos, são previstos os seguintes precipitados nas ligas estudadas: nitreto de titânio (TiN), sulfeto de manganês (MnS), carbonetos de titânio (TiC), carboneto de nióbio (NbC), nitreto de boro (BN), nitreto de alumínio (AlN), carbo-sulfeto de titânio (Ti4C2S2), carboneto de cromo (Cr3C2), cementita (Fe3C) com composição normal e modificada e carboneto de vanádio (VC). O composto TiN será precipitado em temperaturas elevadas (acima de 1400°C) ao passo que o composto VC precipitará em temperaturas de aproximadamente 245°C. O estudo mostrou ainda que o primeiro composto a precipitar-se na maioria das ligas desse estudo foi o sulfeto de manganês (MnS), com exceção de duas ligas onde essa ordem foi alterada pelo carboneto de nióbio (NbC) e pelo carbosulfeto de titânio (Ti4C2S2). Os últimos compostos a precipitarem-se nas ligas avaliadas foram: cementita (Fe3C), carboneto de cromo (Cr3C2) e uma cementita com composição modificada na faixa de temperatura de 80 a 260°C.

 

This work aims to show the types of precipitates formed in low carbon steels microalloyed with Nb addition to manganese and also the sequence of precipitation of this compounds. For the realization of precipitation maps Thermocalc was used in version 5 of Windows (TCFW5) with database Fe in version 6 program (TCFE6). Based on thermodynamic studies, are provided in the following precipitates studied alloys: titianium nitride (TiN), manganese sulfide (MnS), titanium carbide (TiC), niobium carbide (NbC), boron nitride (BN), aluminum nitride (AlN), titanium carbo-sulfide (Ti4C2S2), chromium carbide (Cr3C2), cementite (Fe3C) with normal and modified composition and vanadium carbide (VC). The compound TiN Will precipitate at elevated temperature above 1400°C) whereas the compound VC precipitate at temperatures of approximately 245°C. The study also showed that the fisrt compound to precipitate in most alloys this study was the manganese sulfide (MnS), except fot two alloys where that ordem was modified by niobium carbide (NbC) and carbosulfide titanium (Ti4C2S2). The latter compounds to precipitate on the alloy were evaluated: cementite (Fe3C), chromium carbide (Cr3C2) and cementite with modified composition at the temperature range 80-260°C

Keywords

Thermocalc; Precipitados; Termodinâmica.

Thermocalc; Precipitates; Thermodynamic.