O presente trabalho tem por objetivo determinar através de experimentos características mecânicas de flexão do compósito de matriz polimérica reforçado por fibras de bambu e sisal. As fibras foram cortadas nos comprimentos de 5 mm, 10 mm e 15 mm. As fibras de sisal foram adquiridas no comércio e as de bambu extraídas a partir de plantas da cidade de Belém-PA. Foram fabricados 10 corpos de prova para cada série de compósitos, utilizando matriz de poliéster tereftálica insaturada e pré-acelerada. O tipo de ensaio foi o de flexão em três pontos de acordo com a norma ASTM D790-03, onde se investigaram as superfícies de fraturadas e a influência dos comprimentos de fibras (5 mm, 10 mm e 15 mm) e porcentagem de cada constituintes dos compósitos fabricados nos resultados. O melhor desempenho no referente à carga máxima e resistência a flexão fora o sisal de 10 mm, com 39,6 N de carga e 0,716 MPa de resistência. A segunda melhor amostra fora a de bambu de 5 mm, apresentando carga máxima igual a 26,8 N e resistência a flexão de 0,399 MPa.

This study aims to determine experimentally the mechanical properties of bending in the polymer matrix composite reinforced by fibers of bamboo and sisal. The fibers were cut in lengths of 5 mm, 10 mm and 15 mm. The sisal fibers were acquired in trade and the bamboo extracted from plants of the city of Belem – Brazil. We made 10 specimens for each series of composites using tereftalic unsaturated polyester matrix and pre-accelerated. The type of test that was conducted for the mechanical characterization of the material is the three-point bending according to ASTM standard D790-03, where we investigated the fractured surfaces and the influence of the lengths of fibers (5 mm, 10 mm and 15 mm). The best performance with regard to load and resistance was the sisal 10 mm, with 39.6 N load resistance and 0.716 MPa. The second sample was the best bamboo 5 mm, and maximum load equal to 26.8 N and resistance to bending of 0.399 MPa.

Keywords

Propriedade mecânica; Compósito poliéster; Fibras naturais.

Mechanical properties; Composite polyester; Natural fibers.