Title

PROPRIEDADES DE QUEIMA DE UMA ARGILA CAULINÍTICA COM INCORPORAÇÃO DE FONOLITO

PROPERTIES OF FIRING A KAOLINITIC CLAY WITH INCORPORATION OF PHONOLITH

Authorship

VIEIRA, CARLOS MAURÍCIO FONTES; DELAQUA, GEOVANA CARLA GIRONDI

VIEIRA, CARLOS MAURÍCIO FONTES

I am this author

DELAQUA, GEOVANA CARLA GIRONDI

I am this author

DOI

10.5151/2594-5327-41270

Downloads

Abstract

ESTE TRABALHO TEM POR OBJETIVO AVALIAR O COMPORTAMENTO DE QUEIMA DE UMA ARGILA CAULINíTICA INCORPORADA COM FONOLITO VISANDO à OBTENçãO DE REVESTIMENTO CERâMICO PRENSADO DO TIPO SEMIPOROSO. FORAM PREPARADAS COMPOSIçõES COM ADIçãO DE FONOLITO A UMA ARGILA CAULINíTICA NAS PROPORçõES DE 20 E 40% EM PESO. PARA EFEITO COMPARATIVO, AVALIOU-SE UMA MASSA CERâMICA INDUSTRIAL PROVENIENTE DO PóLO CERâMICO DE SANTA GERTRUDES. FORAM PREPARADOS CORPOS DE PROVA CILíNDRICOS POR PRENSAGEM UNIAXIAL A 25 MPA PARA QUEIMA EM TEMPERATURAS VARIANDO DE 1050 A 1200OC. NAS AMOSTRAS QUEIMADAS, FORAM REALIZADOS ENSAIOS TECNOLóGICOS PARA DETERMINAçãO DA RETRAçãO LINEAR E ABSORçãO DE áGUA EM FUNçãO DA TEMPERATURA DE QUEIMA. A AVALIAçãO MICROESTRUTURAL DAS COMPOSIçõES ESTUDADAS FOI REALIZADA POR DIFRAçãO DE RAIOS-X E MICROSCOPIA ELETRôNICA DE VARREDURA. OS RESULTADOS MOSTRARAM QUE A ADIçãO DE FONOLITO MELHORA SIGNIFICATIVAMENTE A SINTERIZAçãO DA ARGILA CAULINíTICA, SOBRETUDO, EM TEMPERATURAS ACIMA DE 1150OC, ONDE OCORRE UMA REDUçãO BRUSCA DA POROSIDADE. APESAR DO MAIOR TEOR DE óXIDOS ALCALINOS EM COMPARAçãO COM UMA MASSA INDUSTRIAL DE REVESTIMENTO CERâMICO, AS MISTURAS ARGILA/FONOLITO Só ALCANçARAM UMA ABSORçãO DE áGUA DE 10%, MáXIMA PARA REVESTIMENTOS SEMIPOROSOS, EM TEMPERATURAS CERCA DE 80OC SUPERIOR à MASSA INDUSTRIAL.

THIS WORK HAD AS ITS OBJECTIVE TO EVALUATE THE FIRING BEHAVIOR OF A KAOLINITIC CLAY INCORPORATED WITH PHONOLITE AIMING AT SEMIPOROUS PRESSED CERAMIC TILES. COMPOSITIONS WERE PREPARED WITH ADDITION OF 20 AND 40 WT.% OF PHONOLITE TO A KAOLINITIC CLAY. FOR COMPARISON, AN INDUSTRIAL CERAMIC BODY FROM SANTA GERTRUDES, STATE OF SãO PAULO, WAS ALSO EVALUATED. CYLINDRICAL SPECIMENS WERE PREPARED BY UNIAXIAL PRESSURE AT 25 MPA FOLLOWED BY FIRING AT TEMPERATURES VARYING FROM 1050 TO 1200OC. THE FIRED SPECIMENS WERE SUBMITTED TO THE FOLLOWING TESTS: LINEAR SHRINKAGE AND WATER ABSORPTION AS FUNCTION OF THE FIRING TEMPERATURE. THE MICROSTRUCTURAL EVALUATION OF THE COMPOSITIONS WAS ACCOMPLISHED BY X-RAY DIFFRACTION AND SCANNING ELECTRON MICROSCOPY. THE RESULTS SHOWED THAT THE PHONOLITE ADDITION SIGNIFICANTLY IMPROVE THE SINTERING OF THE CLAY, MAINLY, ABOVE 1150OC WITH SHARP DECREASE OF THE POROSITY. ALTHOUGH THE CLAY/PHONOLITE MIXTURES SHOWED HIGHER AMOUNT OF ALKALINE OXIDES AS COMPARED WITH THE INDUSTRIAL CERAMIC TILE BODY, THE REQUIRED WATER ABSORPTION OF 10% FOR SEMIPOROUS TILES WAS ONLY REACHED AT TEMPERATURES AROUND 80OC HIGHER THAN THE INDUSTRIAL BODY

Keywords

Fonolito; Argila caulinítica; Revestimento cerâmico

Phonolite; Kaolinitic cla; Ceramic tiles.