RECICLAGEM DE VIDRO DE LÂMPADA FLUORESCENTE EM CERÂMICA VERMELHA

RECYCLING FLUORESCENT LAMP GLASS IN RED CERAMIC

Authorship

VIEIRA, CARLOS MAURÍCIO FONTES; DELAQUA, GEOVANA CARLA GIRONDI

VIEIRA, CARLOS MAURÍCIO FONTES

I am this author

DELAQUA, GEOVANA CARLA GIRONDI

I am this author

DOI

10.5151/2594-5327-41322

Downloads

Abstract

STE TRABALHO INVESTIGOU A VIABILIDADE DE RECICLAGEM DE VIDRO DE LâMPADA FLUORESCENTE ADICIONADA A UMA MASSA TRADICIONAL DE CERâMICA VERMELHA. FOI FEITA CARACTERIZAçãO POR FRX, DRX, GRANULOMETRIA. FORAM FEITAS FORMULAçõES COM DIFERENTES PERCENTUAIS ADICIONANDO, E PRODUZIDOS CORPOS DE PROVA POR PRENSAGEM, E QUEIMADOS EM DIFERENTES TEMPERATURAS, PARA QUE FOSSE POSSíVEL AVALIAR AS PROPRIEDADES DE ABSORçãO DE áGUA, RETRAçãO LINEAR E TENSãO DE RUPTURA à FLEXãO. COMO OS RESULTADOS FOI POSSíVEL CONCLUIR QUE POR APRESENTAR COMPOSIçãO SIMILAR à ARGILA, A ADIçãO DE VIDRO A UMA MASSA CERâMICA CONTRIBUI PARA MELHORIA DA PLASTICIDADE, E APóS A QUEIMA, REDUçãO NA ABSORçãO DE áGUA E CONSEQUENTEMENTE, AUMENTO NA RESISTêNCIA DAS PEçAS. COM ISTO, A CERâMICA é UMA ALTERNATIVA ALTAMENTE VIáVEL PARA A DESTINAçãO DESTE RESíDUO

THIS WORK INVESTIGATED THE FEASIBILITY OF RECYCLING FLUORESCENT LAMP GLASS ADDED TO A TRADITIONAL RED CERAMIC MASS. CHARACTERIZATION WAS CARRIED OUT BY FRX, DRX, GRANULOMETRY. FORMULATIONS WERE MADE WITH DIFFERENT PERCENTAGES, AND TEST SPECIMENS WERE PRODUCED BY PRESSING AND FIRED AT DIFFERENT TEMPERATURES, SO THAT IT WAS POSSIBLE TO EVALUATE THE PROPERTIES OF WATER ABSORPTION, LINEAR SHRINKAGE AND FLEXURAL RUPTURE STRESS. BASED ON THE RESULTS, IT WAS POSSIBLE TO CONCLUDE THAT, AS IT HAS A COMPOSITION SIMILAR TO CLAY, THE ADDITION OF GLASS TO A CERAMIC MASS CONTRIBUTES TO IMPROVED PLASTICITY, AND AFTER FIRING, A REDUCTION IN WATER ABSORPTION AND, CONSEQUENTLY, AN INCREASE IN THE RESISTANCE OF THE PIECES. THEREFORE, CERAMICS ARE A HIGHLY VIABLE ALTERNATIVE FOR DISPOSING OF THIS WASTE

Keywords

vidro; lâmpada fluorescente; argila; cerâmica

Glass; Fluorescent Lamp; clay; ceramic.