Title

Recozimento da Liga de Alumínio AA 7075 após Laminação a frio

Annealing of aluminum alloy AA 7075 after cold rolling

DOI

10.5151/1516-392X-30121

Downloads

Abstract

A liga de alumínio AA 7075 recebida no estado T6 (conformada e envelhecida artificialmente) sofreu tratamento térmico a 300°C com o objetivo de causar o engrossamento das partículas de MgZn2, intermetálico responsável pelo endurecimento do material. As amostras foram então deformadas 45% em redução de espessura por laminação e recozidas isotermicamente a 200°C e a 250°C por tempos variados para estudar a cinética de amolecimento por meio de medidas de dureza Vickers. Os resultados indicam que a cinética de amolecimento em ambas as temperaturas de recozimento aproxima-se do comportamento previsto pelo modelo Johnson-Mehl-Avrami-Kolmogorov (JMAK) com boa concordância (coeficientes de correlação de 0,9725 e 0,9140 a 200°C e a 250°C, respectivamente), ainda que as micrografias ópticas da amostra recozida a 300°C por 4 horas não evidenciem a ocorrência de recristalização.

 

The aluminum alloy AA 7075-T6 (wrought and artificially aged) was heat treated at 300°C in order to cause the coarsening of the intermetallic MgZn2 particles, that is, the phase which is responsible for the material hardening. The samples were cold - rolled (45% in thickness reduction) and annealed at 200°C and 250°C at different time intervals to study the softening kinetics by Vickers hardness measurements. The results point out that the softening kinetics at both annealing temperatures are well described by the Johnson-Mehl-Avrami-Kolmogorov (JMAK) model with good agreement (correlation coefficients of 0.9725 and 0.9140 for 200°C and 250°C, respectively), even though optical micrographs of the sample annealed at 300°C for 4 hours didn’t show the recrystallization occurrence.

Keywords

Liga de alumínio AA 7075, Superenvelhecimento, Laminação a frio, Amolecimento.

Aluminium alloy AA 7075, Overaging, Cold rolling, Softening.