Title

RECRISTALIZAÇÃO DE RIPAS DE MARTENSITA DURANTE TRATAMENTO TÉRMICO DE REVENIMENTO DE AÇOS BAIXA LIGA E ALTA RESISTÊNCIA

RECRYSTALLIZATION OF MARTENSITE LATHS DURING TEMPERING HEAT TREATMENT OF HIGH-STRENGTH LOW ALLOY STEELS

Authorship

Trindade, Vicente Braz; Silva, Mauro Euclides Samuel da; Rivelli, Bruna Fernandes; Miranda, Raissa Santos; Garcia, Naiara Aparecida Martins; Bartulici, Eric

Trindade, Vicente Braz

I am this author

Silva, Mauro Euclides Samuel da

I am this author

Rivelli, Bruna Fernandes

I am this author

Miranda, Raissa Santos

I am this author

Garcia, Naiara Aparecida Martins

I am this author

Bartulici, Eric

I am this author

DOI

10.5151/1516-392X-259

Downloads

Abstract

Tubos sem costura line-pipe de aço C-Mn têm um importante papel na indústria de extração e transporte de óleo e gás. Estes tubos sofrem diversas solicitações mecânicas em seu uso sendo expostos a diversos meios. Em um dos estágios de fabricação, o tubo passa por um processo de tratamento térmico de têmpera e revenimento, onde adquire propriedades importantes para o seu desempenho. Uma dessas propriedades é a dureza ao longo do corpo e da seção transversal do tubo, que é desejável que tenha valores acima de 180 HV10 e abaixo de 230 HV10. Um desvio no tratamento térmico de revenimento provoca a recristalização da martensita, causando pontos de dureza abaixo de 160 HV10. Este trabalho avaliou em quais condições de tempo e temperatura em que a recristalização ocorre. Esta avaliação foi feita através de análises metalográficas via microscopias ótica e eletrônica de varredura e avaliação da dureza. Foi possível concluir que para temperaturas acima de 665°C, em tempos variados, ocorreu a recristalização da martensita em grãos equiaxiais de ferrita. Leituras de microdureza Vickers permitiram identificar os pontos de dureza com valores abaixo de 160 HV10, que estavam localizados próximos as paredes externa e interna das amostras

Seamless linepipe steels containing low C-Mn play an important role in the oil & gas industry for extraction and transportation. These pipes are submitted to severe mechanical loading as well as exposed to aggressive environments. During manufacturing, usually the pipes are submitted to quenching and tempering heat treatment in order to adjust the mechanical properties and hardness. This last one, is a very important parameter in order to select material for sour service application, therefore, it is usually requested values in the range of 180 HV10 to 230 HV10. However, deviation on the tempering conditions can cause a drop on the hardness lower than 160HV10, due to the recrystallization phenomenon of the martensite. In this paper, it was evaluated the conditions of tempering, time and temperature, for which the recrystallization of the martensite laths occurs. The evaluation was done through metallographic analysis using light and scanning electron microscopy as well as hardness measurements. It was possible to conclude that the recrystallization of martensite for temperature higher than 665°C for different heat treatment times occur. It was observed that the hardness dropped locally on regions close to the inner and outer pipe surface

Keywords

Recristalização da martensita; Baixa dureza; Aços C-Mn; Tratamento térmico

Martensite recrystallization; Low hardness; C-Mn steels; Heat treatment