Title

RECUPERAÇÃO DE TURBINAS HIDRÁULICAS CAVITADAS POR DEPOSIÇÃO DE REVESTIMENTOS A BASE DE COBALTO – ASPECTOS MICROESTRUTURAIS

MICROSTRUCTURAL FEATURES OF AUSTENITIC-COBALT COATING ALLOY USED TO REPAIR CAVITATION EROSION IN TURBINE BLADES

Authorship

Musardo, Gustavo Borges; Araújo, Márcia Regina Vieira de; Yamakami, Wyser José; Ventrella, Vicente Afonso; Gallego, Juno

Musardo, Gustavo Borges

I am this author

Araújo, Márcia Regina Vieira de

I am this author

Yamakami, Wyser José

I am this author

Ventrella, Vicente Afonso

I am this author

Gallego, Juno

I am this author

DOI

10.5151/2594-5327-0279

Downloads

Abstract

Neste trabalho foi investigada a microestrutura de amostras preparadas conforme o procedimento usado no reparo de danos causados por cavitação em turbinas hidráulicas. Foram depositadas por soldagem com proteção gasosa (SAMG) camadas de eletrodos dos tipos E70-S6, E309-T1 e E410NiMo sobre substratos similares aos materiais das turbinas. As camadas exteriores foram preparadas com o uso de um aço inoxidável com adição de cobalto, indicado para reparos que requerem resistência ao desgaste causado pela cavitação. Usando microscopia ótica como técnica de análise foram explorados e discutidos aspectos microestruturais associados às diversas camadas de revestimento e suas possíveis implicações sobre a dureza das mesmas. Verificou-se que tanto a microestrutura quanto as medidas de microdureza foram influenciadas pela composição do eletrodo e pelo ciclo térmico de soldagem aplicado na deposição do revestimento.

The cavitation erosion is one of the main reasons for the damage of flow machines, being responsible for significant loss of mass in their parts. Cobalt-base alloys have been traditionally used in water turbines as an effective hardfacing coating, which are usually deposited by gas metal arc welding (GMAW) process on cavitation erosion surface. In the present work several flux-cored and solid wires, such as AWS E70- S6, E309-T1, E410NiMo and an austenitic stainless steel containing cobalt, were used to make buttering and hardfacing layers. Samples from welding procedures were prepared for microstructure characterization by light microscopy. Vickers microhardness tests have been carried out on these layers, which results have been analysed and discussed with their respective microstructures. It was concluded that austenitic stainless steel with cobalt addition have allowed higher microhardness values but these results were dependent on the kind of substrates or deposited layers and their microstrutural features.

Keywords

Cavitação; Liga ao cobalto; Revestimento soldado; Microestrutura.

Cavitation; Cobalt-austenitic stainless steel; Hardfacing; Microstructure.