RECUPERAÇÃO DO MANGANÊS OBTIDO NA OZONIZAÇÃO DO LIXIVIADO DO MINÉRIO DE NÍQUEL LATERÍTICO E SUA CARACTERIZAÇÃO POR ESPECTROMETRIA

RECUPERATION OF THE MANGANESE OBTAINED IN THE OZONIZATION OF LEACHATE LATERITIC NICKEL AND ITS CHARACTERIZATION BY SPECTROMETRY

DOI

10.5151/2594-357X-31760

Downloads

Abstract

Será descrito o ensaio da recuperação do manganês vindo do lixiviado do minério de níquel laterítico através da oxidação com ozônio de 200 ml de uma solução sintética sulfatada nos pH´s 0,15 e 1,5 e temperatura de 21°C, contendo oito metais (Al 3,4, Co 0,08, Cr 0,17, Fe+3 13,02, Mg 6,36, Mn 0,32, Ni 0,17 e Zn 0,04 g/l) que simula o lixiviado. A solução foi ozonizada em um reator do tipo coluna de bolhas com agitador acoplado a um gerador de ozônio, alimentado por oxigênio 99% na vazão de 1l/min e que funciona pelo método corona. Nos ensaios de ozonização foram coletadas amostras a cada 15 minutos e medido o ORP a cada 10 minutos. No final do ensaio, a solução ozonizada foi decantada, centrifugada, filtrada, separada do sólido e condicionada para análise. A solução sintética, a ozonizada e o filtrado foram caracterizados no espectrômetro de emissão óptica por plasma acoplado indutivamente, o ICP-OES. O melhor potencial de recuperação de manganês ocorreu no pH 1,5 e foi de 74%. Foi obtida na solução final 85 mg/l de Mn+2, valor acima da legislação brasileira, então não deve ser despejada na água, mas poderá ser usada como fonte secundária de manganês.

 

"It will be described the test of the manganese recuperation coming in the leachate lateritic nickel ore through oxidation with ozone of 200 ml sulphated synthetic solution at pH´s 0.15 and 1.5 and temperature 21 °C, containing eight metals (Al 3.4, Co 0.08, Cr 0.17, Fe+3 13.02, Mg 6.36, Mn 0.32, Ni 0.17 and Zn 0.04 g/l) that simulates the leachate. The solution was ozonized in a bubble column type reactor with agitator coupled to an ozone generator, feeded by 99% of oxygen in the 1 l/min flow rate and operated by the corona method. In the ozonization tests samples were collected every 10 minutes and measured the ORP every 10 minutes. At the end of the test, the solution was decanted, centrifuged, filtered, separated from the solid and conditioned for analysis. The synthetic and ozonized solution and the filtrate were characterized in the inductively coupled plasma optical emission spectrometer, the ICP-OES. The best manganese recovery potential occurred at pH 1.5 and was 74%. In the final solution was obtained 85 mg/l of Mn+2, a value above the Brazilian legislation, so it should not be discharged into the water, but it could be used as a secondary source of manganese."

Keywords

Minério de Níquel laterítico; Manganês; Ozônio; Espectrometria

Lateritic Nickel Ore; Manganese; Ozone; Spectrometry

How to refer

Oruê, Beatriz Peralta; Espinosa, Denise Crocce Romano; Tenório, Jorge Alberto Soares. RECUPERAÇÃO DO MANGANÊS OBTIDO NA OZONIZAÇÃO DO LIXIVIADO DO MINÉRIO DE NÍQUEL LATERÍTICO E SUA CARACTERIZAÇÃO POR ESPECTROMETRIA , p. 240-249. In: 19° Simpósio de Mineração, São Paulo, 2018.
ISSN: 2594-357X , DOI 10.5151/2594-357X-31760