REDUÇÃO DO ÍNDICE (%) DE TRINCAS LONGITUDINAIS EM PLACAS DE LC DA GERDAU USINA OURO BRANCO

REDUCTION OF LONGITUDINAL CRACKS RATE (%) IN SLABS FROM CONTINUOS CASTER AT GERDAU OURO BRANCO STEELWORKS

Authorship

Silva, Álvaro Gomes da; Oliveira, Alisson Paulo de; Junior, Alvimar Paes Pinto; Mourão, Bruno de Assis; Carvalho, Carlos Vinícius Domingos de; Storck, Gilberson Mendonça; Filho, Rui Coelho de Assis; Souza, Werlisdarly Carvalho; Silva, Carlos Antônio da; Santos, Gabriel Romeu T

Silva, Álvaro Gomes da

I am this author

Oliveira, Alisson Paulo de

I am this author

Junior, Alvimar Paes Pinto

I am this author

Mourão, Bruno de Assis

I am this author

Carvalho, Carlos Vinícius Domingos de

I am this author

Storck, Gilberson Mendonça

I am this author

Filho, Rui Coelho de Assis

I am this author

Souza, Werlisdarly Carvalho

I am this author

Silva, Carlos Antônio da

I am this author

Santos, Gabriel Romeu T

I am this author

DOI

10.5151/2594-5300-22788

Downloads

Abstract

Ocorrência de Trincas Longitudinais em placas via Lingotamento Contínuo é um problema que importuna há algum tempo os produtores de aço, uma vez que ocasionam perdas de produtividade e sucateamento de algumas peças. O problema está concentrado em aços da família Peritético e Médio Carbono com teores de carbono entre 0,09% e 0,17%. Muitos fatores têm sido atribuídos para a incidência de trincas longitudinais e devido à complexidade do problema, é difícil isolar o parâmetro que mais impacta no aparecimento das trincas, sendo assim, utilizou-se uma equação que ajuda a quantificar o índice de trincas longitudinais chamado “fator F”, com este fator, consegue-se agrupar os parâmetros geométricos do fluxo de aço no Molde em uma única equação. Os resultados foram bastante satisfatórios com uma redução do índice de trincas longitudinais: 29,58% para 0,80% do aço Peritético Micro Ligado (%C: 0,10; %Mn: 1,05%); 15,82% para 1,74% do aço Peritético Micro Ligado (%C: 0,14; %Mn: 1,52%) e 43,59% para 0,0% do aço Médio Carbono Micro Ligado (%C: 0,15; %Mn: 1,38%) e, eliminando o sucateamento de placas.

Occurrence of Longitudinal Cracks in slabs via Continuous Casting has been a troublesome problem for steel producers, since they cause productivity losses and scrapping. The problem is concentrated in both Peritectic Steels and Medium Carbon Steels families with carbon content between 0.09% and 0.17%. Many factors have been attributed to the incidence of longitudinal cracks and due to the complexity of the problem it is difficult to isolate the single parameter that impacts the appearance of cracks. Therefore, an equation was used to help quantifying the index of longitudinal cracking what is called the "F factor". With this factor, it is possible to group the geometric parameters of the steel flow in the mold in just a single equation. The results were quite satisfactory with reduction of longitudinal cracking index: 29.58% to 0.80% for Alloyed Peritectic steel (%C: 0,10; %Mn: 1,05%); 15,82% to 1,74% for Alloyed Peritectic steel (%C:0,14; %Mn:1,52%) and 43,59% to 0,0% for Alloyed Medium Carbon steel (%C:0,15; %Mn:1,38%) and thus eliminating the scrapping of the slabs.

Keywords

Trincas longitudinais; Fluxo de aço; Molde; Fator F.

Longitudinal cracks; Steel flux; Mold; F factor.