Title

REPRODUÇÃO DO ENDURECIMENTO SECUNDÁRIO EM DIFERENTES CONDIÇÕES DE REVENIMENTO DO AÇO FERRAMENTA PARA TRABALHO A FRIO AISI D2

REPRODUCTION OF SECONDARY HARDENING UNDER DIFFERENT TEMPERING CONDITIONS OF AISI D2 COLD WORK TOOL STEEL

Authorship

CONCI, MAYCOLN DEPIANTI; CENTENO, DANY MICHELL ANDRADE; GOLDENSTEIN, HÉLIO; OLIVEIRA, RENE RAMOS DE; FARINA, PAULA FERNANDA DA SILVA

CONCI, MAYCOLN DEPIANTI

I am this author

CENTENO, DANY MICHELL ANDRADE

I am this author

GOLDENSTEIN, HÉLIO

I am this author

OLIVEIRA, RENE RAMOS DE

I am this author

FARINA, PAULA FERNANDA DA SILVA

I am this author

DOI

10.5151/5463-5463-41601

Downloads

Abstract

PARâMETROS SãO UTILIZADOS PARA ESTIMAR RELAçõES ENTRE TEMPO E TEMPERATURA QUE PRODUZEM EFEITOS SIMILARES NO REVENIMENTO. ESTE ESTUDO PROPõE ANALISAR DIFERENTES CONDIçõES DE REVENIMENTO DO AçO FERRAMENTA AISI D2, TEMPERADO A 1040 ºC, E A POSSIBILIDADE DE REPRODUZIR O PICO DE ENDURECIMENTO SECUNDáRIO OBTIDO NO REVENIMENTO CONVENCIONAL, QUE OCORRE A CERCA DE 500 ºC. AO AUMENTAR A TEMPERATURA DE REVENIMENTO PARA 600 ºC, O PARâMETRO HOLLOMON-JAFFE SUGERE TRATAMENTO EM MINUTOS, E PARA 700 ºC, EM SEGUNDOS. OS RESULTADOS, OBTIDOS POR DILATOMETRIA, DIFRAçãO DE RAIOS X, MICROSCOPIA, MEDIçãO DE DUREZA E TENSõES RESIDUAIS, MOSTRAM QUE, NO SUPER-REVENIMENTO A 700 ºC, A PRECIPITAçãO DE CARBONETOS RESULTA EM DUREZA SIMILAR AO RECOZIMENTO, COM MICROESTRUTURA ANáLOGA à RECRISTALIZAçãO. MUDANçAS MICROESTRUTURAIS ALTERAM AS TENSõES RESIDUAIS, MANTENDO A DUREZA NOS REVENIMENTOS ATé 600 ºC, LIMITANDO AS PREVISõES DO PARâMETRO DE HOLLOMON-JAFFE NA REPRODUçãO DA DUREZA SECUNDáRIA NO REVENIDO DO AçO AISI D2.

PARAMETERS ARE USED TO ESTIMATE RELATIONSHIPS BETWEEN TIME AND TEMPERATURE THAT PRODUCE SIMILAR EFFECTS IN TEMPERING. THIS STUDY PROPOSES TO ANALYZE DIFFERENT TEMPERING CONDITIONS OF AISI D2 TOOL STEEL, QUENCHED AT 1040 ºC, AND THE POSSIBILITY OF REPRODUCING THE SECONDARY HARDENING PEAK OBTAINED IN CONVENTIONAL TEMPERING, WHICH OCCURS AT AROUND 500 ºC. INCREASING THE TEMPERING TEMPERATURE TO 600 ºC, THE HOLLOMON-JAFFE PARAMETER SUGGESTS TREATMENT IN MINUTES, AND FOR 700 ºC, IN SECONDS. RESULTS FROM DILATOMETRY, X-RAY DIFFRACTION, MICROSCOPY, HARDNESS MEASUREMENT, AND RESIDUAL STRESS ANALYSIS SHOW THAT AT 700 ºC OVER-TEMPERING, CARBIDE PRECIPITATION RESULTS IN HARDNESS SIMILAR TO ANNEALING, WITH A MICROSTRUCTURE ANALOGOUS TO RECRYSTALLIZATION. MICROSTRUCTURAL CHANGES ALTER RESIDUAL STRESSES, MAINTAINING HARDNESS IN TEMPERING UP TO 600 ºC, LIMITING THE HOLLOMON-JAFFE PARAMETER'S PREDICTIONS IN REPRODUCING SECONDARY HARDNESS IN TEMPERED AISI D2 STEEL.

Keywords

Aço Ferramenta AISI D2; Revenimento; Endurecimento Secundário.

AISI D2 Tool Steel; Tempering; Secondary Hardening.