RESISTÊNCIA MECÂNICA A FRIO E A QUENTE DE PELOTAS AUTORREDUTORAS DE MINÉRIO DE FERRO

MECHANICAL BEHAVIOR OF SELF-REDUCING PELLETS FROM IRON ORE

DOI

10.5151/2594-357X-30370

Downloads

Abstract

Pelotas compostas de minério de ferro, aglomerante e coque foram analisadas quanto à resistência à compressão (a frio e após aqueciemento) e porosidade. Para isso, três lotes de pelotas foram confeccionados, com diferentes teores de redutor, até a quantidade necessária para reação completa com os óxidos de ferro. Após seu preparo, as pelotas passaram por diferentes tempos de cura ao ar. Ensaios de resistência à compressão à frio e porosidade foram realizados em pelotas verdes e com 3, 7, 14, 21 e 28 dias de cura. Após 28 dias, uma série de pelotas foram secas e submetidas a testes de resistência à compressão após serem aquecidas a temperaturas entre 200ºC a 900º. Analisou-se, também, a perda de massa em cada patamar de temperatura. Entre os principais resultados, verificou-se que o comportamento mecânico de pelotas autorredutoras é melhorado com o aumento do tempo de cura e prejudicado pelo aumento do teor de coque e aumento da temperatura. Após 600ºC, a resistência das pelotas cai potencialmente. Além disso, lotes com maiores teores de coque apresentaram maiores valores de porosidade, sendo que este aumento foi mais significativo nos primeiros dias de cura.

 

Composite pellets of Iron ore with binder and coke were analyzed for their cold and hot behaviors, such as compressive strength and porosity. For this, three batches of pellets were prepared, with different reducer contents, until the amount needed for complete reaction with the iron oxides. The amount of binder was set at 8%. After preparation, the pellets were separated into samples that would undergo different curing times in the air. Tests of cold compressive strength and porosity were performed for green pellets and with 3, 7, 14, 21 and 28 of curing days. After 28 days, batches of pellets were dried and subjected to tests of hot compressive strength, varying temperatures from 200ºC to 900º. The mass loss at each temperature plateau was also analyzed. From results, it was verified that the mechanical behavior of self-reducing pellets is improved with the increase of curing time and impaired by the increase of the coke content and increase in temperature. After 600ºC, the resistance of the pellets falls potentially. In addition, batches with higher coke content had higher values of porosity, and this increase was more significant in the first days of cure.

Keywords

Minério de ferro, Autorredutoras, Resistência à compressão, Tempo de cura

Self-reducing, Iron ore, Binder, Hot and cold behaviors, compressive strength, cure