RESISTÊNCIA A FLEXÃO DE COMPÓSITOS DE POLIURETANO REFORÇADOS COM FIBRA DE BAMBU EM DIFERENTES PROPORÇÕES

BENDING RESISTANCE OF POLYURETHANE COMPOSITES REINFORCED WITH BAMBOO FIBER IN DIFFERENT PROPORTIONS

Authorship

LOPES, MARIANA DIAS MACHADO; MEIRELES, ALEXANDRE AUGUSTO MACIEL RANGEL; SIMONASSI, NOAN TONINI; LOPES, FELIPE PERISSE DUARTE; MONTEIRO, SERGIO NEVES

LOPES, MARIANA DIAS MACHADO

I am this author

MEIRELES, ALEXANDRE AUGUSTO MACIEL RANGEL

I am this author

SIMONASSI, NOAN TONINI

I am this author

LOPES, FELIPE PERISSE DUARTE

I am this author

MONTEIRO, SERGIO NEVES

I am this author

DOI

10.5151/2594-5327-41237

Downloads

Abstract

COMPóSITOS REFORçADOS POR FIBRAS NATURAIS SãO PESQUISADOS E UTILIZADOS POR DéCADAS DEVIDO A UMA SéRIE DE CARACTERíSTICAS VANTAJOSAS, TAIS COMO, BOAS PROPRIEDADES MECâNICAS, BAIXO CUSTO DE PRODUçãO, BAIXA DENSIDADE O QUE LEVA A UM PRODUTO FINAL DE BAIXO PESO. NESTE ARTIGO, é APRESENTADA UMA ANáLISE ABRANGENTE SOBRE A RESISTêNCIA A FLEXãO DE COMPóSITOS DE POLIURETANO REFORçADOS COM FIBRAS DE BAMBU EM DIFERENTES PROPORçõES. NO âMBITO DESTE ESTUDO, FORAM PRODUZIDOS COMPóSITOS DE POLIURETANO COM 60, 70, 80 E 90% DE FIBRAS DE BAMBU, SENDO ENTãO AVALIADA SUA RESISTêNCIA à FLEXãO POR ENSAIO DE 3 PONTOS. OS RESULTADOS INDICARAM UMA INFLUêNCIA CONSIDERáVEL DA PROPORçãO DE FIBRAS DE BAMBU UTILIZADAS, SENDO VERIFICADO UM AUMENTO SUBSTANCIAL NO MóDULO DE RUPTURA DAS AMOSTRAS DE 60% PARA 90% EM VOLUME DE FIBRA BAMBU INCORPORADA, DE 79,61 MPA PARA 142,40 MPA RESPECTIVAMENTE, DEMONSTRANDO UMA TENDêNCIA GERAL DE AUMENTO DA RESISTêNCIA à MEDIDA QUE HOUVE O INCREMENTO DE FIBRA. ESSA PESQUISA PROPORCIONA PERSPECTIVAS VALIOSAS PARA O APRIMORAMENTO DE COMPóSITOS DE POLIURETANO EM APLICAçõES QUE DEMANDAM ELEVADA RESISTêNCIA à FLEXãO.

COMPOSITES REINFORCED BY NATURAL FIBERS HAVE BEEN RESEARCHED AND USED FOR DECADES DUE TO A SERIES OF ADVANTAGEOUS CHARACTERISTICS, SUCH AS GOOD MECHANICAL PROPERTIES, LOW PRODUCTION COST, LOW DENSITY, WHICH LEADS TO A LOW WEIGHT FINAL PRODUCT. IN THIS ARTICLE, A COMPREHENSIVE ANALYSIS IS PRESENTED ON THE FLEXURAL RESISTANCE OF POLYURETHANE COMPOSITES REINFORCED WITH BAMBOO FIBERS IN DIFFERENT PROPORTIONS. WITHIN THE SCOPE OF THIS STUDY, POLYURETHANE COMPOSITES WITH 60, 70, 80, AND 90% BAMBOO FIBERS WERE PRODUCED, AND THEIR FLEXURAL STRENGTH WAS THEN EVALUATED THROUGH A 3-POINT TEST. THE RESULTS INDICATED A CONSIDERABLE INFLUENCE OF THE PROPORTION OF BAMBOO FIBERS USED, WITH A SUBSTANTIAL INCREASE IN THE RUPTURE MODULUS OF THE SAMPLES FROM 60% TO 90% IN VOLUME OF INCORPORATED BAMBOO FIBER, FROM 73,61 MPA TO 142.40 MPA RESPECTIVELY, DEMONSTRATING A GENERAL TREND OF INCREASING STRENGTH AS THE FIBER CONTENT INCREASED. THIS RESEARCH PROVIDES VALUABLE INSIGHTS FOR THE ENHANCEMENT OF POLYURETHANE COMPOSITES IN APPLICATIONS REQUIRING HIGH FLEXURAL STRENGTH.

Keywords

Compósitos de poliuretano; fibra de bambu; resistência a flexão; propriedades mecânicas.

Poliurethane composites; bamboo fiber; flexural strength; mechanical properties.