RESISTÊNCIA À FLEXÃO DE COMPÓSITOS DE MATRIZ POLIURETANA DERIVADA DE ÓLEO DE MAMONA REFORÇADOS COM FIBRA DE EMBIRA

BENDING STRENGTH OF POLYURETHANE MATRIX COMPOSITES DERIVED FROM CASTOR OIL REINFORCED WITH EMBIRA FIBER

Authorship

MAGALHÃES, MARCÔNIO PEREIRA DE

MAGALHÃES, MARCÔNIO PEREIRA DE

I am this author

DOI

10.5151/2594-5327-41253

Downloads

Abstract

O PRESENTE ESTUDO VISA INVESTIGAR A VIABILIDADE DO EMPREGO INDUSTRIAL DA FIBRA DE EMBIRA, PROVENIENTE DA ENTRECASCA/CASCA DA EMBIRA-BRANCA (DAPHNOPSIS UTILIS), áRVORE DA MATA ATLâNTICA, COMO REFORçO EM COMPóSITOS DE MATRIZ POLIMéRICA, CONSTITUíDA POR RESINA POLIURETANA - PU, DERIVADA DO óLEO DE MAMONA. PORTANTO, COMPóSITOS REFORçADOS COM 50%, 60%, 70%, 80% E 90% DE FRAçãO MáSSICA DE EMBIRA FORAM FABRICADOS E SUBMETIDOS A ENSAIOS DE FLEXãO, CURVATURA EM 3 PONTOS. OS RESULTADOS MOSTRAM QUE, MESMO COM O AUMENTO DAS FRAçõES MáSSICAS DE EMBIRA, FOI MANTIDA CONSTANTE A PROPRIEDADE MECâNICA DE RESISTêNCIA ESPECíFICA à FLEXãO DOS COMPóSITOS. NO ENTANTO, O MóDULO DE ELASTICIDADE ESPECíFICA, NA FLEXãO DOS COMPóSITOS, COM 50% DE REFORçO ALCANçOU 7,65 MPA.CM³/G, MAIOR VALOR MéDIO, CLASSIFICADO COMO GRUPO (A), ENQUANTO QUE OS DE 60% E 70% DE REFORçO, POR NãO APRESENTAREM DIFERENçAS ESTATíSTICAS SIGNIFICATIVAS DE SUAS MéDIAS, CLASSIFICADOS COMO GRUPO (B) APRESENTOU A MENOR MéDIA, APENAS CERCA DE 30% DA RIGIDEZ DO COMPóSITO (A); E, OS REFORçADOS COM 70%, 80% E 90%, GRUPO (C) POR NãO APRESENTAREM TAMBéM DIFERENçAS ESTATíSTICAS SIGNIFICATIVAS DE SUAS MéDIAS, COM CERCA 43% DA RIGIDEZ DO GRUPO (A), SENDO A FRAçãO DE 70% DE REFORçO COMUM A AMBOS OS GRUPOS, (B) E (C).

THE PRESENT STUDY AIMS TO INVESTIGATE THE INDUSTRIAL FEASIBILITY OF USING EMBIRA FIBER, DERIVED FROM THE INNER BARK OF THE EMBIRA-BRANCA (DAPHNOPSIS UTILIS) TREE FROM THE ATLANTIC FOREST, AS REINFORCEMENT IN POLYMER MATRIX COMPOSITES MADE OF POLYURETHANE RESIN (PU) DERIVED FROM CASTOR OIL. THEREFORE, COMPOSITES REINFORCED WITH 50%, 60%, 70%, 80%, AND 90% MASS FRACTIONS OF EMBIRA WERE MANUFACTURED AND SUBJECTED TO THREE-POINT BENDING TESTS. THE RESULTS SHOW THAT EVEN WITH INCREASING EMBIRA MASS FRACTIONS, THE SPECIFIC FLEXURAL STRENGTH OF THE COMPOSITES REMAINED CONSTANT. HOWEVER, THE SPECIFIC MODULUS OF ELASTICITY IN FLEXURE FOR THE COMPOSITES WITH 50% REINFORCEMENT REACHED 7.65 MPA.CM³/G, THE HIGHEST AVERAGE VALUE, CLASSIFIED AS GROUP (A). IN CONTRAST, THOSE WITH 60% AND 70% REINFORCEMENT, SHOWING NO STATISTICALLY SIGNIFICANT DIFFERENCES IN THEIR MEANS, WERE CLASSIFIED AS GROUP (B) AND HAD THE LOWEST AVERAGE, ONLY ABOUT 30% OF THE STIFFNESS OF COMPOSITE (A). COMPOSITES REINFORCED WITH 70%, 80%, AND 90%, CLASSIFIED AS GROUP (C), ALSO SHOWED NO STATISTICALLY SIGNIFICANT DIFFERENCES IN THEIR MEANS, WITH ABOUT 43% OF THE STIFFNESS OF GROUP (A), WITH THE 70% REINFORCEMENT FRACTION COMMON TO BOTH GROUPS (B) AND (C).

Keywords

Embira; Resina Poliuretana, Compósito Poliméricos; Resistência à Flexão

Embira; Polyurethane Resin; Polymer Composite; Bending Strenght