SELEÇÃO DE VARIÁVEIS DE ENSAIO DE DESGASTE PARA AÇO FERRAMENTA EM ESTAMPAGEM A QUENTE

SELECTION OF WEAR TESTING VARIABLES FOR HOT STAMPING TOOL STEEL

Authorship

PINTAUDE, GIUSEPPE; ARIETA, FRANCISCO; BREGANON, ROGÉRIO

PINTAUDE, GIUSEPPE

I am this author

ARIETA, FRANCISCO

I am this author

BREGANON, ROGÉRIO

I am this author

DOI

10.5151/5463-5463-40584

Downloads

Abstract

ESTE TRABALHO APRESENTA A INFLUêNCIA DOS PARâMETROS CARGA, TEMPO E TEMPERATURA NO COMPORTAMENTO TRIBOLóGICO DO AçO FERRAMENTA PARA ESTAMPAGEM A QUENTE DIN 1.2344 (X40CRMOV5-1) APóS OS TRATAMENTOS TéRMICOS DE TêMPERA EM BANHO DE SAIS, COM TEMPERATURA DE AUSTENITIZAçãO EM 1050°C E TRIPLO REVENIMENTO PARA VALOR DE DUREZA DE 54,1HRC. OS ENSAIOS DE DESGASTE FORAM CONDUZIDOS UTILIZANDO UM TRIBôMETRO NA CONFIGURAçãO DE DESLIZAMENTO ALTERNATIVO, NãO LUBRIFICADO, COM FREQUêNCIA DE 5HZ, CARGAS DE 25, 50 E 75N, TEMPOS DE 15, 30 E 60 MINUTOS, E TEMPERATURAS DE 200, 300 E 400°C, ALéM DA TEMPERATURA AMBIENTE. COMO CONTRA-CORPO FORAM UTILIZADAS ESFERAS DE ALTA ALUMINA DE 5MM DE DIâMETRO. AS TRILHAS FORAM AVALIADAS ATRAVéS DE MICROSCOPIA ELETRôNICA DE VARREDURA E INTERFEROMETRIA. OS RESULTADOS DOS ENSAIOS MOSTRARAM QUE O ENSAIO COM CARGA DE 25N, TEMPERATURA DE 200°C E TEMPO DE 60 MINUTOS FAVORECEU UM MELHOR SUPORTE DE CARGA EM FUNçãO DO ACúMULO DE DEBRIS E DA FORMAçãO DA CAMADA DE óXIDO MAIS COMPACTA.

THIS STUDY SHOWS THE INFLUENCE OF LOAD, TIME, AND TEMPERATURE VARIABLES ON THE TRIBOLOGICAL BEHAVIOR OF HOT STAMPING TOOL STEEL DIN 1.2344 (X40CRMOV5-1) AFTER HEAT TREATMENTS IN A SALT BATH, WITH AUSTENITIZATION TEMPERATURE AT 1050°C AND TRIPLE TEMPERING FOR HARDNESS VALUE OF 54.1HRC. WEAR TESTS WERE CONDUCTED USING A TRIBOMETER IN DRY RECIPROCATING SLIDING CONFIGURATION, WITH A FREQUENCY OF 5HZ, LOADS OF 25, 50, AND 75N, TESTING TIMES OF 15, 30, AND 60 MINUTES, AND TEMPERATURES OF 200, 300 AND 400°C, BESIDES THE ROOM TEMPERATURE. AS THE COUNTERBODY 5-MM DIAMETER HIGH ALUMINA BALLS WERE USED. THE TRACKS WERE EVALUATED USING SCANNING ELECTRON MICROSCOPY AND INTERFEROMETRY. THE RESULTS SHOWED THAT THE TEST WITH A 25 N LOAD, A TEMPERATURE OF 200°C, AND A TIME OF 60 MINUTES FAVORED BETTER LOAD SUPPORT DUE TO THE DEBRIS ACCUMULATION AND THE FORMATION OF A MORE COMPACT OXIDE LAYER.

Keywords

aço DIN 1.2344; Ensaio de deslizamento; Óxidos.

DIN 1.2344 steel; Sliding wear; Oxides.