Title

SINTERIZAÇÃO DE WBN E ADITIVOS EM ALTAS PRESSÕES E ALTAS TEMPERATURAS

WBN AND ADDITIVES SINTERING IN HIGH PRESSURE AND HIGH TEMPERATURES

Authorship

Campos, Mariane Abreu Alves; Almeida, Luciana Lezira Pereira de; Skury, Ana Lúcia Diegues; Monteiro, Sergio Neves

Campos, Mariane Abreu Alves

I am this author

Almeida, Luciana Lezira Pereira de

I am this author

Skury, Ana Lúcia Diegues

I am this author

Monteiro, Sergio Neves

I am this author

DOI

10.5151/1516-392X-27136

Downloads

Abstract

A utilização do wBN como ferramenta de usinagem pode eliminar a necessidade de retífica das peças. Portanto, neste trabalho, os experimentos realizados tiveram por objetivo o estudo e caracterização de compósitos à base de wBN, diboreto de titânio (TiB2) e alumínio (Al) para obtenção de pastilhas para usinagem. A composição utilizada para a investigação utilizou 70% de wBN. Os compósitos foram obtidos sob altas pressões e altas temperaturas via aplicação cíclica . As patilhas atingiram aproximadamente 4,5 mm de diâmetro, e altura de 4,0 mm. As amostras foram caracterizadas por ensaio de dureza Vickers, microscopia eletrônica de varredura, microscopia confocal e densidade. De forma geral, os melhores resultados foram para amostras com ciclos de um minuto cada, para os três ciclos, sendo pouco dependente do valor da pressão aplicada. Foi observada dureza maior que 17GPa, baixa porosidade e um valor de densidade aparente muito próxima à teórica.

Inserts of the wBN-based are indispensable for high-precision and high speed machining of ferrous materials and the use of wBN as machining tool can eliminate the need for grinding parts. Therefore, in this paper, the experiments aimed to the study and characterization of composites with boron nitride wurtzítico (wBN), titanium diboride (TiB2) and aluminum (Al) to obtain inserts for the machining. The composition used for this investigation utilized 70% WBN. The composites obtained under high pressure and high temperature by cycling applications these parameters were sintered at different temperatures and pressures, from three different time cycles. The consolidated reached approximately 4.5 mm in diameter and 4.0 mm height. The samples were characterized by Vickers hardness testing, scanning electron microscopy, confocal microscopy and density test. In general, the best results for samples were with cycles of one minute each, for three cycles, with little dependence on the applied pressure value. We observed a higher hardness than 17GPa, low porosity and apparent density value near to the theoretical, than have indicated optimum properties for the compact, considerations demonstrated by microscopy. The results showed composites produced from sintering and efficient samples with attractive properties.

Keywords

Sinterização, Nitreto wurtzítico de boro, Usinagem

Sintering, Wurtzite boron nitride, Machining