Title

SÍNTESE DE PÓS COMPÓSITOS DE NiCrAl-Al2O3 UTILIZANDO MOAGEM DE ALTA ENERGIA

SYNTHESIS OF NiCrAl-Al2O3 COMPOSITE POWDERS USING HIGH-ENERGY MILLING

DOI

10.5151/2594-5300-14978

Downloads

Abstract

Pós compósitos de NiCrAl-Al2O3 foram produzidos utilizando moagem de energia e pós de NiO, Cr e Al como reagentes. Duas composições foram preparadas: (1) 3NiO:3Cr:5,5Al; (2) 3NiO:0,903Cr:2,679Al. As composições foram homogeneizadas por 1 h e então processadas em moinho Spex CertPrep 8000M mixer/mill. As moagens foram conduzidas por diversos tempos, sob atmosfera de argônio, utilizando um poder de moagem igual a 7:1. Os produtos das moagens foram caracterizados através de difratometria de raios X (DRX), microscopia eletrônica de varredura (SEM) e análise térmica diferencial (DTA). Os difratogramas de raios X mostraram a formação de Ni3Al e Al2O3 após a Mistura 2 ter sido moída por 120 min.

 

NiCrAl-Al2O3 composite powders were produced using high-energy milling and NiO, Cr and Al powders as starting materials. Two compositions were prepared: (1) 3NiO:3Cr:5.5Al; (2) 3NiO:0.903Cr:2.679Al. The compositions were homogenized for 1h, and then milled in a Spex CertiPrep 8000M mixer/mill. The millings were conducted for several times, under argon atmosphere, and a ball-to-powder ratio of 7:1 were used. The as-milled powders were characterized using X-ray diffraction (DRX), scanning electron microscopy (SEM) and differential thermal analysis (DTA). DRX results showed the formation of Ni3Al and Al2O3 after Blend 2 have been milled for 120 min.

Keywords

NiCrAl-Al2O3; Moagem de alta energia; Aluminotermia.

NiCrAl-Al2O3; High-energy milling; Aluminothermy.