SÍNTESE DE ZEÓLITAS “A” A PARTIR DO RESÍDUO CAULÍNITICO AMAZÔNICO*

SYNTHESIS OF ZEOLITE 'A' FROM AMAZONIAN KAOLINITIC RESIDUE

Authorship

AMORIM, RIAN CRISTIAN DOURO; MODESTO, ANTÔNIO LUCAS ALCANTARA; RUIVO, ALEX GABRIEL OLIVEIRA; SOUZA, ANA PAULA SOUZA DE; ESTUMANO, DIEGO CARDOSO; COSTA, DEIBSON SILVA DA; RODRIGUES, EMERSON CARDOSO

AMORIM, RIAN CRISTIAN DOURO

I am this author

MODESTO, ANTÔNIO LUCAS ALCANTARA

I am this author

RUIVO, ALEX GABRIEL OLIVEIRA

I am this author

SOUZA, ANA PAULA SOUZA DE

I am this author

ESTUMANO, DIEGO CARDOSO

I am this author

COSTA, DEIBSON SILVA DA

I am this author

RODRIGUES, EMERSON CARDOSO

I am this author

DOI

10.5151/2594-4711-41408

Downloads

Abstract

O PRESENTE TRABALHO OBJETIVOU SINTETIZAR ZEóLITAS "4A" A PARTIR DO REJEITO DE CAULIM E APLICAR O PRODUTO SINTETIZADO EM TROCA IôNICA. PARA A SíNTESE DA ZEóLITA 4A, O REJEITO FOI CALCINADO A 700°C POR DUAS HORAS PARA SUA TRANSFORMAçãO EM METACAULIM. APóS A CALCINAçãO, O METACAULIM E A SOLUçãO DE NAOH FORAM INTRODUZIDOS EM UM SISTEMA DE SíNTESE, REGULADO PARA TEMPERATURA DE 100°C E VELOCIDADE DE ROTAçãO DE 700 RPM DURANTE 30 MINUTOS. PARA A TROCA IôNICA, UTILIZOU-SE O MESMO SISTEMA DE SíNTESE, A 100°C E 700 RPM, COM A ZEóLITA 4A E A SOLUçãO DE CACL2 POR 8 HORAS. NO PROCEDIMENTO ANALíTICO, O REJEITO DE CAULIM, O METACAULIM E AS ZEóLITAS FORAM SUBMETIDOS à MICROSCOPIA ELETRôNICA DE VARREDURA (MEV) E DIFRAçãO DE RAIOS X (DRX). AS MICROGRAFIAS DAS ZEóLITAS CONFIRMARAM A PRESENçA DE MORFOLOGIA CúBICA, A QUAL é CARACTERíSTICA DE ZEóLITAS DO TIPO A. OS DIFRATOGRAMAS, ATRAVéS DAS FICHAS CONSULTADAS, CONFIRMARAM A PRESENçA DE CRISTAIS ZEOLíTICOS, DE ACORDO COM O OBSERVADO NO MEV. DESTA FORMA, O REJEITO DE CAULIM SE APRESENTOU COMO UM MATERIAL VIáVEL PARA A FORMAçãO DE CRISTAIS ZEOLíTICOS DO TIPO A, OS QUAIS APRESENTAM A PROPRIEDADE DE TROCA IôNICA, CONFIRMADA PELA FORMAçãO DE ZEóLITAS 5A.

THE PRESENT WORK AIMED TO SYNTHESIZE "4A" ZEOLITES FROM KAOLIN WASTE AND APPLY THE SYNTHESIZED PRODUCT IN ION EXCHANGE. FOR THE SYNTHESIS OF 4A ZEOLITE, THE WASTE WAS CALCINED AT 700°C FOR TWO HOURS TO TRANSFORM IT INTO METAKAOLIN. AFTER CALCINATION, THE METAKAOLIN AND NAOH SOLUTION WERE INTRODUCED INTO A SYNTHESIS SYSTEM, REGULATED TO A TEMPERATURE OF 100°C AND A ROTATION SPEED OF 700 RPM FOR 30 MINUTES. FOR ION EXCHANGE, THE SAME SYNTHESIS SYSTEM WAS USED, AT 100°C AND 700 RPM, WITH 4A ZEOLITE AND CACL2 SOLUTION FOR 8 HOURS. IN THE ANALYTICAL PROCEDURE, THE KAOLIN WASTE, METAKAOLIN, AND ZEOLITES WERE SUBJECTED TO SCANNING ELECTRON MICROSCOPY (SEM) AND X-RAY DIFFRACTION (XRD). THE MICROGRAPHS OF THE ZEOLITES CONFIRMED THE PRESENCE OF CUBIC MORPHOLOGY, WHICH IS CHARACTERISTIC OF TYPE A ZEOLITES. THE DIFFRACTOGRAMS, BASED ON THE CONSULTED DATA SHEETS, CONFIRMED THE PRESENCE OF ZEOLITIC CRYSTALS, AS OBSERVED IN THE SEM. THUS, KAOLIN WASTE PROVED TO BE A VIABLE MATERIAL FOR THE FORMATION OF TYPE A ZEOLITIC CRYSTALS, WHICH EXHIBIT ION EXCHANGE PROPERTIES, CONFIRMED BY THE FORMATION OF 5A ZEOLITES.

Keywords

Caulim; Metacaulim; Troca Iônica

kaolin, Metakaolin, Ion Exchange