Title

SÍNTESE E CARACTERIZAÇÃO DAS LIGAS Cu-Al-Ag E Cu-Ni-Ag

SYNTHESIS AND CHARACTERIZATION OF ALLOYS Cu-Al-Ag AND Cu-Ni-Ag

Authorship

Junior, Renato Pereira da Silva; Monteiro, Waldemar Alfredo; Carrió, Juan Alfredo Guevara

Junior, Renato Pereira da Silva

I am this author

Monteiro, Waldemar Alfredo

I am this author

Carrió, Juan Alfredo Guevara

I am this author

DOI

10.5151/2594-4711-23504

Downloads

Abstract

Neste trabalho foram sintetizadas amostras de ligas metálicas ternárias com Cu-Al- Ag e Cu-Ni-Ag e ligas binárias de Cu-Ag, todas por metalurgia do pó. As ligas receberam tratamento térmico de sinterização e foram caracterizadas metalograficamente. Medidas de microdureza e resistência elétrica foram realizadas nas diferentes composições sintetizadas. As amostras de composições 80%Cu- 10%Al-10%Ag e 80%Cu-10%Ni-10%Ag apresentaram respectivamente condutividades elétricas de 26,3% IACS e 55,0% IACS. As medidas de microdureza foram, respectivamente, 836,32 MPa e 517,33 MPa, representando alta resistência mecânica, o que indica um adequado tratamento térmico para estas composições. Os difratogramas de raios x das ligas sinterizadas mostram as reflexões dos componentes puros e nenhuma presença detectável de óxidos. O tamanho de grão para estas amostras encontram-se entre 15 e 25 μm.

In this paper were synthesized samples of metal alloys with ternary Cu-Al-Ag and Cu- Ni-Ag and binary alloys with Cu-Ag, all by powder metallurgy. The alloys were given a sintering thermal treatment and were characterized metallographically. Measurements of electrical resistance and microhardness were performed in the different compositions synthesized. The samples of compositions 80%Cu-10%Al- 10%Ag and 80%Cu-10%Ni-10%Ag respectively showed the electrical conductivity of 26.3% IACS and 55.0% IACS. Microhardness measurements were, respectively, and 836.32 MPa 517.33 MPa, representing high mechanical strength, which indicates an adequate heat treatment for these compositions. The x rays powder diffraction data of all sintered samples show the reflections of the pure components and no detectable presence of oxides. The grain size for these samples is between 15 and 25 μm.

Keywords

Liga cobre-alumínio-prata; Liga cobre-níquel-prata; Condutividade elétrica; Propriedade mecânica.

Copper-aluminum-silver alloy; Copper-nickel-silver alloy; Electrical conductivity; Mechanical property.