SOBRE A CARACTERIZAÇÃO MICROESTRUTURAL DOS FERROS FUNDIDOS BRANCOS ALTO CROMO E MOLIBDÊNIO

ON THE MICROSTRUCTURAL CHARACTERIZATION OF HIGH CHROMIUM-MOLYBDENIUM WHITE CAST IRON

Authorship

Carvalho, Sandro Mauro de; Macedo, Marcelo Camargo Severo de; Mello, José Daniel Biasoli de; Scandian, Cherlio

DOI

10.5151/2594-5327-0372

Downloads

heading.download_article_detail 81 Downloads

Abstract

Foram estudadas cinco famílias de ligas com relação Cr/C=10 e teores de molibdênio iguais a 0, 3, 6 e 9 % em peso, sendo que para cada família de liga foram elaboradas três composições hipoeutéticas (16, 20 e 24% Cr), uma eutética (28% Cr) e uma hipereutética (32% Cr). Com o objetivo de avaliar o efeito do Cr e do Mo nas ligas, foram realizados ensaios de dureza, difração de raios-X, metalografia quantitativa e qualitativa (microscopia óptica e eletrônica de varredura). As fases encontradas nas ligas isentas de Mo foram ferrita e/ou martensita mais M7C3 para as hipoeutéticas e ferrita mais carboneto M7C3 nas ligas eutéticas e hipereutéticas. A adição de Mo nas composições hipoeutéticas favorece a formação das fases M6C e austenita. Já as ligas de composição eutética, hipereutética e a liga com 24% Cr e 9 % Mo apresentaram a formação dos dois tipos de carboneto em matriz de ferrita.

 

Five kind of alloys were studied with different molybdenum contents (0, 3, 6 and 9 wt%) and a fixed Cr/C ratio (=10). For each molybdenum content 3 hypoeutectic (16, 20 and 24 wt% Cr), 1 eutectic (28 wt% Cr) and 1 hypereutectic (32 %wt Cr) alloys were elaborated. The effect of Cr and Mo contents were evaluated with different techniques (hardness, X rays diffraction, optical microscopy and SEM). Only two phases were found in the Mo free alloys, the matrix and M7C3 carbide. The matrix of two hypoeutectic compositions (16 and 20 wt% Cr) is ferrite and for 24 wt% Cr is martensite. For the eutectic and hypereutectic alloys, the matrix is ferrite. Besides the presence of M7C3 carbide and ferrite, the Mo addition to the hypoeutectic alloys favors the formation of M6C and austenite phases. On the other hand, the 24 wt% Cr (with 9 wt% Mo) alloy, the eutectic and hypereutectic compositions show the presence of the two carbides and ferrite matrix.

Keywords

Ferro fundido branco ao cromo; Molibdênio; Microestrutura.

High chromium white cast iron; Molybdenum; Microstructure.