Title

TEXTURA CRISTALOGRÁFICA E PROPRIEDADES MECÂNICAS DOS AÇOS INOXIDÁVEIS DUPLEX UNS S31803 E UNS S32304 APÓS LAMINAÇÃO A FRIO E RECOZIMENTO

ANALYSIS OF STEEL CRYSTALLOGRAPHIC TEXTURE STAINLESS DUPLEX UNS S31803 AND UNS S32304 AFTER ROLLING COLD TREATMENT AND THERMAL ANNEALING

Authorship

Karina Aparecida Martins Barcelos Gonçalves; Tarcísio Reis de Oliveira; Dagoberto Brandão Santos

Karina Aparecida Martins Barcelos Gonçalves

I am this author

Tarcísio Reis de Oliveira

I am this author

Dagoberto Brandão Santos

I am this author

DOI

10.5151/12abinox-26717

Downloads

Abstract

Amostras dos aços inoxidáveis duplex UNS S31803 (duplex padrão) e UNS S32304 (lean duplex) foram investigadas no estado de fornecimento, após laminação a frio com redução de 64% e 62% e recozimento na temperatura de 1055ºC com 20s de encharque. Foram medidas a dureza Vickers e a quantificação das fases, austenita e ferrita, usando o método de contagem por pontos. A textura cristalográfica foi obtida via técnica de EBSD. A textura cristalográfica da fase ferrítica no estado de fornecimento e recozida apresentou as fibras a <011>//DL e q {100} //DN mais intensas, enquanto a fibra g {111} //DN aparece com intensidade menor. Na fase austenítica as principais componentes encontradas com maior intensidade estão na fibra a <011>//DN e na fibra b com menor intensidade.

Samples of duplex stainless steel 31803 (standard duplex) and 32304 (lean duplex) were investigated in the as-received state, cold rolling with a reduction of 64% and 62% and after annealing at 1055ºC for 20 s soaking. Mechanical property was evaluated by hardness measurements. Quantification of austenite and ferrite volume fraction was done by point counting method. Crystallographic texture was obtained via EBSD technique. Crystallographic texture of ferrite phase in as-received condition and annealed were more intense in alpha fiber <011> // DL and tetha fiber {100} // ND. Meanwhile, gamma fiber {111} // DN appears with less intensity. In the austenitic phase the greater intensity are found in the alpha fiber <011> // ND, and beta fiber to a lesser intensity.

Keywords

Aço inoxidável duplex; Textura cristalográfica; Laminação a frio; Recozimento

Duplex stainless steel; Crystallographic texture; Cold rolling; Annealing