Title

UNIÃO DE CHAPAS DE COBRE E LATÃO PELO FRICTION STIR WELDING (FSW)

JOINING OF COPPER AND BRASS PLATES THROUGH FRICTION STIR WELDING (FSW)

Authorship

DINIZ, SAULO BRINCO; FREIRE, JOHN SANTOS; REIS, LUCAS MOURA MONTENEGRO; PEIXOTO, IGOR DE OLIVEIRA JERONIMO; SOUZA, TALITA GAMA DE; MONTEIRO, SÉRGIO NEVES

DINIZ, SAULO BRINCO

I am this author

FREIRE, JOHN SANTOS

I am this author

REIS, LUCAS MOURA MONTENEGRO

I am this author

PEIXOTO, IGOR DE OLIVEIRA JERONIMO

I am this author

SOUZA, TALITA GAMA DE

I am this author

MONTEIRO, SÉRGIO NEVES

I am this author

DOI

10.5151/2594-5327-40906

Downloads

Abstract

O COBRE E O LATãO POSSUEM COEFICIENTE DE EXPANSãO E CONDUTIVIDADE TéRMICA ALTOS, APRESENTANDO LIMITAçõES DURANTE A SOLDAGEM POR FUSãO, E DESTA FORMA, O FRICTION STIR WELDING (FSW) SE DESTACA. ESTE ESTUDO TESTOU A SOLDABILIDADE DE CHAPAS DE COBRE E LATãO COM 3,17 MM DE ESPESSURA, UTILIZANDO O FSW COM TRêS VELOCIDADES DE ROTAçãO DISTINTAS E DEMAIS PARâMETROS CONSTANTES. FORAM REALIZADAS INSPEçõES VISUAIS, ANáLISE MICROESTRUTURAL E MONITORAMENTO DA TEMPERATURA. OS RESULTADOS INDICARAM QUE UMA VELOCIDADE DE ROTAçãO MAIOR RESULTOU EM UMA MELHOR APARêNCIA DO CORDãO DE SOLDA, EMBORA TENHA AUMENTADO A EXTENSãO DA REGIãO OXIDADA. ALéM DISSO, A TEMPERATURA VARIOU ENTRE 75 E 250 °C, DIRETAMENTE RELACIONADA à VELOCIDADE DE ROTAçãO E AO COMPRIMENTO DA CAMADA OXIDADA PARA O COBRE. TODAS AS AMOSTRAS APRESENTARAM DEFEITOS NA SEçãO TRANSVERSAL.

COPPER AND BRASS HAVE A HIGH COEFFICIENT OF EXPANSION AND THERMAL CONDUCTIVITY, PRESENTING LIMITATIONS DURING FUSION WELDING, AND IN THIS WAY, FRICTION STIR WELDING (FSW) STANDS OUT. THIS STUDY TESTED THE WELDABILITY OF 3.17 MM THICK COPPER AND BRASS SHEETS USING FSW WITH THREE DIFFERENT ROTATION SPEEDS AND CONSTANT PARAMETERS. FOR THIS PURPOSE, VISUAL INSPECTIONS, MICROSTRUCTURAL ANALYSIS AND TEMPERATURE MONITORING. THE RESULTS INDICATED THAT A HIGHER ROTATION SPEED RESULTED IN A BETTER APPEARANCE OF THE WELD BEAD, ALTHOUGH IT INCREASED THE EXTENT OF THE OXIDIZED REGION. ADDITIONALLY, THE TEMPERATURE RANGED FROM 75 TO 250 °C, DIRECTLY RELATED TO THE ROTATION SPEED AND THE LENGTH OF THE OXIDIZED LAYER. ALL SAMPLES SHOWED DEFECTS IN THE CROSS SECTION.

Keywords

Cobre; Latão; Friction Stir Welding; Soldagem.

Copper; Brass; Friction Stir Welding; Welding.